Find suppliers for this alloy
C64752
| Elements | |||||
|---|---|---|---|---|---|
| Cu(1) | Sn | P | Ni | Si | |
|
(1) Cu + Sum of Named Elements, 99.92% min. |
|||||
| Min (%) | 0.15 | 0.005 | 2.8 | 0.6 | |
| Max (%) | Rem | 1.0 | 0.05 | 3.8 | 1.2 |
| Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.2% Offset (ksi) |
Elongation (%) |
Vickers Hardness, 3000 gm |
|---|---|---|---|---|---|---|
| * Measured at room temperature, 68°F (20°C). | ||||||
| Strip | Extra Hard | H06 |
120 Min 128 Typ 135 Max |
116 Min 124 Typ 132 Max |
1 Min |
265 Typ |
| Hard | H04 |
113 Min 120 Typ 127 Max |
110 Min 116 Typ 125 Max |
5 Min |
252 Typ |
|
| Spring | H08 |
127 Min 136 Typ 145 Max |
123 Min 132 Typ 142 Max |
1 Min |
290 Typ |
|
| Melting Point - Liquidus°F | 1972 |
|---|---|
| Melting Point - Solidus°F | 1930 |
| Densitylb/cu in. at 68°F | 0.318 |
| Specific Gravity | 8.86 |
| Electrical Conductivity% IACS at 68°F | 32 |
| Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 89 |
| Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 9.61 |
| Modulus of Elasticity in Tensionksi | 18900 |
| Poisson's Ratio | 0.33 |
| Technique | Suitability |
|---|---|
| Soldering | Excellent |
| Brazing | Excellent |
| Oxyacetylene Welding | Good |
| Gas Shielded Arc Welding | Good |
| Coated Metal Arc Welding | Good |
| Spot Weld | Excellent |
| Seam Weld | Excellent |
| Butt Weld | Excellent |
| Capacity for Being Cold Worked | Excellent |
| Capacity for Being Hot Formed | Fair |
Common Fabrication Processes
No fabrication process properties for this alloy
Thermal Properties
No thermal properties for this alloy
Typical Uses
No information for this alloy
Applicable Specifications
No applicable specifications for this alloy
Corrosion Properties
No Corrosion Properties Available.