Find suppliers for this alloy
C64760
Elements | |||||||
---|---|---|---|---|---|---|---|
Cu(1,2) | Pb | Sn | Zn | Ni(3) | Mg | Si | |
(1) Cu value includes Ag. (2) Cu + Sum of Named Elements 99.5% min. (3) Ni value includes Co. |
|||||||
Min (%) | 93.5 | 0.20 | 0.40 | 0.05 | |||
Max (%) | 0.02 | 0.30 | 2.5 | 2.5 | 0.05 | 0.6 |
Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.2% Offset (ksi) |
Elongation (%) |
Vickers Hardness, 500 gm | Fatigue Strength** (ksi) |
Proportional Limit (ksi) |
Section Size (in) |
---|---|---|---|---|---|---|---|---|---|
* Measured at room temperature, 68°F (20°C). ** Fatigue Strength: 100 x 106 cycles, unless indicated as [N] x 106. | |||||||||
Flat Products | 1/2 Hard | H02 |
83 Typ |
75 Typ |
10 Typ |
178 Typ |
58 Typ | ||
Extra Hard | H06 |
104 Typ |
94 Typ |
7 Typ |
215 Typ |
78 Typ | |||
Hard | H04 |
97 Typ |
87 Typ |
10 Typ |
202 Typ |
36 Typ | 59 Typ | 0.009 |
Melting Point - Liquidus°F | 1989 |
---|---|
Melting Point - Solidus°F | 1954 |
Densitylb/cu in. at 68°F | 0.321 |
Specific Gravity | 8.9 |
Electrical Conductivity% IACS at 68°F | 47 |
Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 113.9 |
Specific Heat CapacityBtu/ lb /°F at 68°F | 0.09 |
Modulus of Elasticity in Tensionksi | 12700 |
Modulus of Rigidityksi | 4800 |
Technique | Suitability |
---|---|
Soldering | Excellent |
Brazing | Good |
Gas Shielded Arc Welding | Good |
Spot Weld | Good |
Capacity for Being Cold Worked | Excellent |
Capacity for Being Hot Formed | Excellent |
Machinability Rating | 20 |
Common Fabrication Processes
Treatment | Minimum* | Maximum* | ||
---|---|---|---|---|
* Temperature is measured in Fahrenheit. | ||||
Annealing | 842 | |||
Hot Working Temperature | 1472 | 1742 | ||
Stress Relief | 482 |
Typical Uses
Applicable Specifications
Corrosion Properties