C64775
| Elements | ||||||||||
|---|---|---|---|---|---|---|---|---|---|---|
| Cu(1,2) | Pb | Sn | Zn | Fe | Ni(3) | Cr | Mg | Mn | Si | |
|
(1) Cu value includes Ag. (2) Cu + Sum of Named Elements 99.5% min. (3) Ni value includes Co. |
||||||||||
| Min (%) | 0.05 | 0.30 | 1.5 | 0.40 | ||||||
| Max (%) | Rem | 0.05 | 1.0 | 0.8 | 0.10 | 3.5 | 0.50 | 0.30 | 0.10 | 0.9 |
| Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.5% Ext (ksi) |
Elongation (%) |
Vickers Hardness, 500 gm |
|---|---|---|---|---|---|---|
| * Measured at room temperature, 68°F (20°C). | ||||||
| Flat Products | Hard | H04 |
106 Min 115 Typ 120 Max |
98 Min 107 Typ |
7 Typ |
240 Typ |
| Melting Point - Solidus°F | 1956 |
|---|---|
| Densitylb/cu in. at 68°F | 0.32 |
| Specific Gravity | 8.8 |
| Electrical Conductivity% IACS at 68°F | 38 |
| Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 91 |
| Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 9.7 |
| Specific Heat CapacityBtu/ lb /°F at 68°F | 0.09 |
| Modulus of Elasticity in Tensionksi | 19100 |
| Poisson's Ratio | 0.33 |
| Technique | Suitability |
|---|---|
| Soldering | Excellent |
| Brazing | Not Recommended |
| Oxyacetylene Welding | Not Recommended |
| Gas Shielded Arc Welding | Not Recommended |
| Coated Metal Arc Welding | Not Recommended |
| Spot Weld | Not Recommended |
| Seam Weld | Not Recommended |
| Butt Weld | Not Recommended |
| Capacity for Being Cold Worked | Not Recommended |
| Capacity for Being Hot Formed | Not Recommended |
Common Fabrication Processes
No fabrication process properties for this alloy
Thermal Properties
No thermal properties for this alloy
Typical Uses
No information for this alloy
Applicable Specifications
No applicable specifications for this alloy
Corrosion Properties
No Corrosion Properties Available.