C64775
Elements | ||||||||||
---|---|---|---|---|---|---|---|---|---|---|
Cu(1,2) | Pb | Sn | Zn | Fe | Ni(3) | Cr | Mg | Mn | Si | |
(1) Cu value includes Ag. (2) Cu + Sum of Named Elements 99.5% min. (3) Ni value includes Co. |
||||||||||
Min (%) | 0.05 | 0.30 | 1.5 | 0.40 | ||||||
Max (%) | Rem | 0.05 | 1.0 | 0.8 | 0.10 | 3.5 | 0.50 | 0.30 | 0.10 | 0.9 |
Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.5% Ext (ksi) |
Elongation (%) |
Vickers Hardness, 500 gm |
---|---|---|---|---|---|---|
* Measured at room temperature, 68°F (20°C). | ||||||
Flat Products | Hard | H04 |
106 Min 115 Typ 120 Max |
98 Min 107 Typ |
7 Typ |
240 Typ |
Melting Point - Solidus°F | 1956 |
---|---|
Densitylb/cu in. at 68°F | 0.32 |
Specific Gravity | 8.8 |
Electrical Conductivity% IACS at 68°F | 38 |
Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 91 |
Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 9.7 |
Specific Heat CapacityBtu/ lb /°F at 68°F | 0.09 |
Modulus of Elasticity in Tensionksi | 19100 |
Poisson's Ratio | 0.33 |
Technique | Suitability |
---|---|
Soldering | Excellent |
Brazing | Not Recommended |
Oxyacetylene Welding | Not Recommended |
Gas Shielded Arc Welding | Not Recommended |
Coated Metal Arc Welding | Not Recommended |
Spot Weld | Not Recommended |
Seam Weld | Not Recommended |
Butt Weld | Not Recommended |
Capacity for Being Cold Worked | Not Recommended |
Capacity for Being Hot Formed | Not Recommended |
Common Fabrication Processes
Thermal Properties
Typical Uses
Applicable Specifications
Corrosion Properties