C65680
| Elements | ||||||||||
|---|---|---|---|---|---|---|---|---|---|---|
| Cu(1) | Pb | Sn | Zn | Fe | P | Ni | Al | Mn | Si | |
|
(1) Cu + Sum of Named Elements 99.2% min. |
||||||||||
| Min (%) | 84.0 | 7.0 | 0.05 | 0.01 | 2.5 | |||||
| Max (%) | 0.09 | 0.30 | 11.0 | 0.30 | 0.15 | 0.10 | 0.30 | 0.09 | 4.5 | |
| Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.2% Offset (ksi) |
Elongation (%) |
Vickers Hardness, 3000 gm |
|---|---|---|---|---|---|---|
| * Measured at room temperature, 68°F (20°C). | ||||||
| Bar | As Hot Extruded | M30 |
60.9 Typ |
10 Min |
125 Typ |
|
| Hot Extruded and Annealed | O30 |
40.6 Typ |
20.3 Typ |
20 Min |
80 Typ |
|
| Rod | As Hot Extruded | M30 |
60.9 Typ |
36.3 Typ |
10 Min |
125 Typ |
| Hot Extruded and Annealed | O30 |
36.3 Typ |
17.4 Typ |
20 Min |
80 Typ |
|
| Hot Forged and Annealed | O20 |
37.7 Typ |
18.9 Typ |
20 Min |
80 Typ |
|
| Rod & Bar | As Hot Forged - Air Cooled | M10 |
60.9 Typ |
34.8 Typ |
10 Min |
125 Typ |
| Melting Point - Liquidus°F | 1778 |
|---|---|
| Melting Point - Solidus°F | 1652 |
| Densitylb/cu in. at 68°F | 0.302 |
| Specific Gravity | 8.35 |
| Electrical Conductivity% IACS at 68°F | 7.8 |
| Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 50.4 |
| Technique | Suitability |
|---|---|
| Soldering | Good |
| Brazing | Good |
| Oxyacetylene Welding | Good |
| Gas Shielded Arc Welding | Good |
| Coated Metal Arc Welding | Good |
| Spot Weld | Good |
| Seam Weld | Good |
| Butt Weld | Good |
| Capacity for Being Cold Worked | Good |
| Capacity for Being Hot Formed | Good |
| Forgeability Rating | 80 |
| Machinability Rating | 70 |
Common Fabrication Processes
No fabrication process properties for this alloy
Thermal Properties
No thermal properties for this alloy
Typical Uses
No information for this alloy
Applicable Specifications
No applicable specifications for this alloy
Corrosion Properties
No Corrosion Properties Available.