C65680
Elements | ||||||||||
---|---|---|---|---|---|---|---|---|---|---|
Cu(1) | Pb | Sn | Zn | Fe | P | Ni | Al | Mn | Si | |
(1) Cu + Sum of Named Elements 99.2% min. |
||||||||||
Min (%) | 84.0 | 7.0 | 0.05 | 0.01 | 2.5 | |||||
Max (%) | 0.09 | 0.30 | 11.0 | 0.30 | 0.15 | 0.10 | 0.30 | 0.09 | 4.5 |
Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.2% Offset (ksi) |
Elongation (%) |
Vickers Hardness, 3000 gm |
---|---|---|---|---|---|---|
* Measured at room temperature, 68°F (20°C). | ||||||
Bar | As Hot Extruded | M30 |
60.9 Typ |
10 Min |
125 Typ |
|
Hot Extruded and Annealed | O30 |
40.6 Typ |
20.3 Typ |
20 Min |
80 Typ |
|
Rod | As Hot Extruded | M30 |
60.9 Typ |
36.3 Typ |
10 Min |
125 Typ |
Hot Extruded and Annealed | O30 |
36.3 Typ |
17.4 Typ |
20 Min |
80 Typ |
|
Hot Forged and Annealed | O20 |
37.7 Typ |
18.9 Typ |
20 Min |
80 Typ |
|
Rod & Bar | As Hot Forged - Air Cooled | M10 |
60.9 Typ |
34.8 Typ |
10 Min |
125 Typ |
Melting Point - Liquidus°F | 1778 |
---|---|
Melting Point - Solidus°F | 1652 |
Densitylb/cu in. at 68°F | 0.302 |
Specific Gravity | 8.35 |
Electrical Conductivity% IACS at 68°F | 7.8 |
Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 50.4 |
Technique | Suitability |
---|---|
Soldering | Good |
Brazing | Good |
Oxyacetylene Welding | Good |
Gas Shielded Arc Welding | Good |
Coated Metal Arc Welding | Good |
Spot Weld | Good |
Seam Weld | Good |
Butt Weld | Good |
Capacity for Being Cold Worked | Good |
Capacity for Being Hot Formed | Good |
Forgeability Rating | 80 |
Machinability Rating | 70 |