C66200
Elements | |||||||
---|---|---|---|---|---|---|---|
Cu(1,2) | Pb | Sn | Zn | Fe | P | Ni(3) | |
(1) Cu + Sum of Named Elements 99.5% min. (2) Cu value includes Ag. (3) Ni value includes Co. |
|||||||
Min (%) | 86.6 | 0.20 | 0.05 | 0.30 | |||
Max (%) | 91.0 | 0.05 | 0.7 | Rem | 0.05 | 0.20 | 1.0 |
Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.2% Offset (ksi) |
Elongation (%) |
---|---|---|---|---|---|
* Measured at room temperature, 68°F (20°C). | |||||
Flat Products |
85 Typ |
80 Typ |
5 Typ |
||
1/2 Hard and Stress Relieved | HR02 |
65 Typ |
60 Typ |
15 Typ |
|
Hard and Stress Relieved | HR04 |
75 Typ |
70 Typ |
8 Typ |
Melting Point - Liquidus°F | 1954 |
---|---|
Melting Point - Solidus°F | 1881 |
Densitylb/cu in. at 68°F | 0.318 |
Specific Gravity | 8.8 |
Electrical Conductivity% IACS at 68°F | 35 |
Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 87 |
Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 10 |
Specific Heat CapacityBtu/ lb /°F at 68°F | 0.09 |
Modulus of Elasticity in Tensionksi | 17400 |
Modulus of Rigidityksi | 6700 |
Magnetic Permeability | 0.99 |
Poisson's Ratio | 0.3 |
Technique | Suitability |
---|---|
Capacity for Being Cold Worked | Excellent |
Capacity for Being Hot Formed | Excellent |
Common Fabrication Processes
Treatment | Minimum* | Maximum* | ||
---|---|---|---|---|
* Temperature is measured in Fahrenheit. | ||||
Annealing | 480 | 1110 | ||
Hot Working Temperature | 1200 | 1750 |
Typical Uses
Applicable Specifications
Corrosion Properties