C66710
Elements | ||||||||||
---|---|---|---|---|---|---|---|---|---|---|
Cu(1) | Pb | Sn | Zn | Fe | P | Ni | Co | Mn | Si | |
(1) Cu + Sum of Named Elements 99.5% min. |
||||||||||
Min (%) | 65.0 | 0.10 | 1.0 | |||||||
Max (%) | 70.0 | 0.05 | 0.05 | Rem | 0.05 | 0.30 | 0.05 | 0.05 | 3.0 | 0.05 |
Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.2% Offset (ksi) |
Elongation (%) |
Vickers Hardness, 3000 gm |
---|---|---|---|---|---|---|
* Measured at room temperature, 68°F (20°C). | ||||||
Strip | Annealed | O61 |
50 Min 54 Typ 60 Max |
16 Min 21 Typ 27 Max |
30 Min |
80 Min 100 Max |
Hard | H04 |
68 Min 74 Typ 80 Max |
60 Min 65 Typ 70 Max |
1 Min |
150 Min |
Melting Point - Liquidus°F | 1716 |
---|---|
Melting Point - Solidus°F | 1648 |
Densitylb/cu in. at 68°F | 0.301 |
Specific Gravity | 8.34 |
Electrical Conductivity% IACS at 68°F | 14 |
Electrical Resistivityohm.cmil/ft at 68°F | 68 |
Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 47 |
Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 9.87 |
Modulus of Elasticity in Tensionksi | 15950 |
Poisson's Ratioksi | 0.33 |
Technique | Suitability |
---|---|
Soldering | Poor |
Brazing | Fair |
Oxyacetylene Welding | Poor |
Gas Shielded Arc Welding | Fair |
Coated Metal Arc Welding | Fair |
Spot Weld | Fair |
Seam Weld | Fair |
Butt Weld | Fair |
Capacity for Being Cold Worked | Excellent |
Capacity for Being Hot Formed | Excellent |
Forgeability Rating | 99 |
Machinability Rating | 65 |
Common Fabrication Processes
Typical Uses
Applicable Specifications
Corrosion Properties