Find suppliers for this alloy
C66907
| Elements | ||||||||||
|---|---|---|---|---|---|---|---|---|---|---|
| Cu(1) | Pb | Sn | Zn | Fe | P | Ni | Co | Mn | Si | |
|
(1) Cu + Sum of Named Elements 99.9% min. |
||||||||||
| Min (%) | 8.0 | 0.20 | 8.0 | |||||||
| Max (%) | Rem | 0.05 | 0.05 | 10.0 | 0.05 | 0.8 | 0.05 | 0.05 | 10.0 | 0.05 |
| Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.2% Offset (ksi) |
Elongation (%) |
Vickers Hardness, 3000 gm |
|---|---|---|---|---|---|---|
| * Measured at room temperature, 68°F (20°C). | ||||||
| Strip | 1/2 Hard | H02 |
57 Min 64 Typ 71 Max |
49 Min 54 Typ 60 Max |
8 Min |
150 Min |
| Annealed | O61 |
53 Min 59 Typ 65 Max |
25 Min 30 Typ 35 Max |
30 Min |
100 Min 130 Max |
|
| Hard | H04 |
75 Min 85 Typ 95 Max |
75 Min 80 Typ 85 Max |
1 Min |
170 Min |
|
| Melting Point - Liquidus°F | 1787 |
|---|---|
| Melting Point - Solidus°F | 1652 |
| Densitylb/cu in. at 68°F | 0.308 |
| Specific Gravity | 8.53 |
| Electrical Conductivity% IACS at 68°F | 6 |
| Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 19 |
| Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 9.87 |
| Modulus of Elasticity in Tensionksi | 15240 |
| Poisson's Ratio | 0.33 |
| Technique | Suitability |
|---|---|
| Soldering | Poor |
| Brazing | Fair |
| Oxyacetylene Welding | Poor |
| Gas Shielded Arc Welding | Fair |
| Coated Metal Arc Welding | Fair |
| Spot Weld | Fair |
| Seam Weld | Fair |
| Butt Weld | Fair |
| Capacity for Being Cold Worked | Excellent |
| Capacity for Being Hot Formed | Excellent |
| Forgeability Rating | 99 |
| Machinability Rating | 60 |
Common Fabrication Processes
No fabrication process properties for this alloy
Thermal Properties
No thermal properties for this alloy
Typical Uses
No information for this alloy
Applicable Specifications
No applicable specifications for this alloy
Corrosion Properties
No Corrosion Properties Available.