C66907
Elements | ||||||||||
---|---|---|---|---|---|---|---|---|---|---|
Cu(1) | Pb | Sn | Zn | Fe | P | Ni | Co | Mn | Si | |
(1) Cu + Sum of Named Elements 99.9% min. |
||||||||||
Min (%) | 8.0 | 0.20 | 8.0 | |||||||
Max (%) | Rem | 0.05 | 0.05 | 10.0 | 0.05 | 0.8 | 0.05 | 0.05 | 10.0 | 0.05 |
Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.2% Offset (ksi) |
Elongation (%) |
Vickers Hardness, 3000 gm |
---|---|---|---|---|---|---|
* Measured at room temperature, 68°F (20°C). | ||||||
Strip | 1/2 Hard | H02 |
57 Min 64 Typ 71 Max |
49 Min 54 Typ 60 Max |
8 Min |
150 Min |
Annealed | O61 |
53 Min 59 Typ 65 Max |
25 Min 30 Typ 35 Max |
30 Min |
100 Min 130 Max |
|
Hard | H04 |
75 Min 85 Typ 95 Max |
75 Min 80 Typ 85 Max |
1 Min |
170 Min |
Melting Point - Liquidus°F | 1787 |
---|---|
Melting Point - Solidus°F | 1652 |
Densitylb/cu in. at 68°F | 0.308 |
Specific Gravity | 8.53 |
Electrical Conductivity% IACS at 68°F | 6 |
Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 19 |
Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 9.87 |
Modulus of Elasticity in Tensionksi | 15240 |
Poisson's Ratio | 0.33 |
Technique | Suitability |
---|---|
Soldering | Poor |
Brazing | Fair |
Oxyacetylene Welding | Poor |
Gas Shielded Arc Welding | Fair |
Coated Metal Arc Welding | Fair |
Spot Weld | Fair |
Seam Weld | Fair |
Butt Weld | Fair |
Capacity for Being Cold Worked | Excellent |
Capacity for Being Hot Formed | Excellent |
Forgeability Rating | 99 |
Machinability Rating | 60 |