C67500
| Elements | |||||||
|---|---|---|---|---|---|---|---|
| Cu(1,2) | Pb | Sn | Zn | Fe | Al | Mn | |
|
(1) Cu value includes Ag. (2) Cu + Sum of Named Elements 99.5% min. |
|||||||
| Min (%) | 57.0 | 0.50 | 0.8 | 0.05 | |||
| Max (%) | 60.0 | 0.20 | 1.5 | Rem | 2.0 | 0.25 | 0.50 |
| Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.5% Ext (ksi) |
Elongation (%) |
Rockwell B scale | Shear Strength (ksi) |
Section Size (in) |
Cold Work (%) |
|---|---|---|---|---|---|---|---|---|---|
| * Measured at room temperature, 68°F (20°C). | |||||||||
| Rod | 1/2 Hard | H02 |
84 Typ |
60 Typ |
19 Typ |
90 Typ |
48 Typ |
1 | 20 |
| 1/4 Hard | H01 |
72 Typ |
42 Typ |
27 Typ |
77 Typ |
44 Typ |
2 | 10 | |
| 1/4 Hard | H01 |
77 Typ |
45 Typ |
23 Typ |
83 Typ |
47 Typ |
1 | 10 | |
| Soft Anneal | O60 |
65 Typ |
30 Typ |
33 Typ |
65 Typ |
42 Typ |
1 | ||
| Melting Point - Liquidus°F | 1630 |
|---|---|
| Melting Point - Solidus°F | 1590 |
| Densitylb/cu in. at 68°F | 0.302 |
| Specific Gravity | 8.36 |
| Electrical Conductivity% IACS at 68°F | 24 |
| Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 61 |
| Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 11.8 |
| Specific Heat CapacityBtu/ lb /°F at 68°F | 0.09 |
| Modulus of Elasticity in Tensionksi | 15000 |
| Modulus of Rigidityksi | 5600 |
| Technique | Suitability |
|---|---|
| Soldering | Excellent |
| Brazing | Excellent |
| Oxyacetylene Welding | Good |
| Gas Shielded Arc Welding | Fair |
| Coated Metal Arc Welding | Not Recommended |
| Spot Weld | Good |
| Seam Weld | Fair |
| Butt Weld | Good |
| Capacity for Being Cold Worked | Poor |
| Capacity for Being Hot Formed | Excellent |
| Forgeability Rating | 80 |
| Machinability Rating | 30 |
Common Fabrication Processes
- Hot Forging and Pressing
- hot heading and upsetting
| Treatment | Minimum* | Maximum* | ||
|---|---|---|---|---|
| * Temperature is measured in Fahrenheit. | ||||
| Annealing | 800 | 1100 | ||
| Hot Working Temperature | 1150 | 1450 | ||
| Product Category | Product | Reason Category | Reason |
|---|---|---|---|
| Automotive | Clutch Disks | Corrosion Resistance | Corrosion Resistance |
| Clutch Disks | Friction & Wear Properties | Wear Resistance | |
| Clutch Disks | Mechanical Properties | Fatigue Strength | |
| Clutch Disks | Mechanical Properties | Moderate Strength | |
| Pump Rods | Corrosion Resistance | Corrosion Resistance | |
| Pump Rods | Friction & Wear Properties | Wear Resistance | |
| Pump Rods | Mechanical Properties | Moderate Strength | |
| Shafting | Corrosion Resistance | Corrosion Resistance | |
| Shafting | Friction & Wear Properties | Wear Resistance | |
| Shafting | Mechanical Properties | Moderate Strength | |
| Fasteners | Bolts | Corrosion Resistance | Corrosion Resistance |
| Bolts | Mechanical Properties | Moderate Strength | |
| Industrial | Aircraft Parts | Corrosion Resistance | Corrosion Resistance |
| Aircraft Parts | Friction & Wear Properties | Wear Resistance | |
| Aircraft Parts | Mechanical Properties | Moderate Strength | |
| Balls | Corrosion Resistance | Corrosion Resistance | |
| Balls | Mechanical Properties | Fatigue Strength | |
| Balls | Mechanical Properties | Moderate Strength | |
| Bushings | Corrosion Resistance | Corrosion Resistance | |
| Bushings | Friction & Wear Properties | Wear Resistance | |
| Bushings | Mechanical Properties | Moderate Strength | |
| Valve Bodies | Corrosion Resistance | Corrosion Resistance | |
| Valve Bodies | Friction & Wear Properties | Wear Resistance | |
| Valve Bodies | Mechanical Properties | Moderate Strength | |
| Valve Stems | Corrosion Resistance | Corrosion Resistance | |
| Valve Stems | Friction & Wear Properties | Wear Resistance | |
| Valve Stems | Mechanical Properties | Moderate Strength | |
| Marine | Hardware | Corrosion Resistance | Corrosion Resistance |
| Hardware | Corrosion Resistance | Corrosion Resistance to Fresh Water | |
| Hardware | Corrosion Resistance | Corrosion Resistance to Salt Water | |
| Hardware | Friction & Wear Properties | Wear Resistance | |
| Hardware | Mechanical Properties | Moderate Strength |
| Form | Specific Sub-Form | Application | System | Standard | Description |
|---|---|---|---|---|---|
| Bar | ASTM | B124/B124M | COPPER AND COPPER-ALLOY FORGING ROD, BAR AND SHAPES | ||
| SAE | J461 | WROUGHT AND CAST COPPER ALLOYS | |||
| ASTM | B138/B138M | MANGANESE BRONZE ROD, BAR AND SHAPES | |||
| SAE | J463 | WROUGHT COPPER AND COPPER ALLOYS | |||
| Bolts | ASTM | F468 | NONFERROUS BOLTS, HEX CAP SCREWS, AND STUDS FOR GENERAL USE | ||
| Die | Forgings | SAE | J461 | WROUGHT AND CAST COPPER ALLOYS | |
| Forgings | SAE | J463 | WROUGHT COPPER AND COPPER ALLOYS | ||
| Forgings, Die (Hot Pressed) | ASME | SB283 | COPPER AND COPPER ALLOY DIE FORGINGS (HOT PRESSED) | ||
| ASTM | B283/B283M | COPPER AND COPPER ALLOY DIE FORGINGS (HOT PRESSED) | |||
| Nuts | ASTM | F467 | NONFERROUS NUTS FOR GENERAL USE | ||
| Rod | Forgings | ASTM | B124/B124M | COPPER AND COPPER-ALLOY FORGING ROD, BAR AND SHAPES | |
| SAE | J461 | WROUGHT AND CAST COPPER ALLOYS | |||
| ASTM | B138/B138M | MANGANESE BRONZE ROD, BAR AND SHAPES | |||
| SAE | J463 | WROUGHT COPPER AND COPPER ALLOYS | |||
| Screws | ASTM | F468 | NONFERROUS BOLTS, HEX CAP SCREWS, AND STUDS FOR GENERAL USE | ||
| Shapes | SAE | J463 | WROUGHT COPPER AND COPPER ALLOYS | ||
| ASTM | B124/B124M | COPPER AND COPPER-ALLOY FORGING ROD, BAR AND SHAPES | |||
| SAE | J461 | WROUGHT AND CAST COPPER ALLOYS | |||
| ASTM | B138/B138M | MANGANESE BRONZE ROD, BAR AND SHAPES | |||
| Studs | ASTM | F468 | NONFERROUS BOLTS, HEX CAP SCREWS, AND STUDS FOR GENERAL USE |
Corrosion Properties
No Corrosion Properties Available.