Find suppliers for this alloy
C67600
| Elements | ||||||
|---|---|---|---|---|---|---|
| Cu(1,2) | Pb | Sn | Zn | Fe | Mn | |
|
(1) Cu value includes Ag. (2) Cu + Sum of Named Elements 99.5% min. |
||||||
| Min (%) | 57.0 | 0.50 | 0.50 | 0.40 | 0.05 | |
| Max (%) | 60.0 | 1.0 | 1.5 | Rem | 1.3 | 0.50 |
| Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.5% Ext (ksi) |
Elongation (%) |
Rockwell B scale | Section Size (in) |
|---|---|---|---|---|---|---|---|
| * Measured at room temperature, 68°F (20°C). | |||||||
| Rod | 1/2 Hard | H02 |
84 Typ |
60 Typ |
19 Min |
90 Typ |
1 |
| 1/4 Hard | H01 |
72 Typ |
42 Typ |
27 Min |
77 Typ |
2 | |
| 1/4 Hard | H01 |
77 Typ |
45 Typ |
23 Min |
83 Typ |
1 | |
| Soft Anneal | O60 |
65 Typ |
30 Typ |
33 Min |
65 Typ |
||
| Melting Point - Liquidus°F | 1630 |
|---|---|
| Melting Point - Solidus°F | 1590 |
| Densitylb/cu in. at 68°F | 0.302 |
| Electrical Conductivity% IACS at 68°F | 24 |
| Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 61 |
| Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 11.8 |
| Modulus of Elasticity in Tensionksi | 15000 |
| Modulus of Rigidityksi | 5600 |
| Technique | Suitability |
|---|---|
| Soldering | Excellent |
| Brazing | Excellent |
| Oxyacetylene Welding | Good |
| Gas Shielded Arc Welding | Fair |
| Spot Weld | Good |
| Capacity for Being Cold Worked | Poor |
| Capacity for Being Hot Formed | Excellent |
| Forgeability Rating | 80 |
| Machinability Rating | 60 |
Common Fabrication Processes
No fabrication process properties for this alloy
Thermal Properties
No thermal properties for this alloy
| Product Category | Product | Reason Category | Reason |
|---|---|---|---|
| Industrial | Gate Valve Stems | Corrosion Resistance | Corrosion Resistance |
| Gate Valve Stems | Machining Characteristics | Machinability | |
| Gate Valve Stems | Mechanical Properties | High Strength | |
| Valve Balls | Corrosion Resistance | Corrosion Resistance | |
| Valve Balls | Friction & Wear Properties | Wear Resistance | |
| Valve Balls | Machining Characteristics | Machinability | |
| Welding Rod | Conductivity (Electrical) | Electrical Conductivity | |
| Welding Rod | Corrosion Resistance | Oxidation Resistance |
| Form | Specific Sub-Form | Application | System | Standard | Description |
|---|---|---|---|---|---|
| Brazing Filler Metal | AWS | A5.8 | BRAZING FILLER METAL | ||
| Die Forging | Hot-Pressed | ASTM | B138/B138M | MANGANESE BRONZE ROD, BAR AND SHAPES | |
| Forgings, Die (Hot Pressed) | ASTM | B283/B283M | COPPER AND COPPER ALLOY DIE FORGINGS (HOT PRESSED) | ||
| ASME | SB283 | COPPER AND COPPER ALLOY DIE FORGINGS (HOT PRESSED) | |||
| Rod, Bar & Shapes | ASTM | B124/B124M | COPPER AND COPPER-ALLOY FORGING ROD, BAR AND SHAPES |
Corrosion Properties
No Corrosion Properties Available.