C68370
| Elements | |||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Cu(1) | Pb | Sn | Zn | Fe | P | Ni | Bi | Cd | Mn | Sb | Si | Se | |
|
(1) Cu + Sum of Named Elements 99.7% min. |
|||||||||||||
| Min (%) | 60.5 | 0.01 | 0.7 | ||||||||||
| Max (%) | 65.0 | 0.10 | 0.30 | Rem | 0.20 | 0.10 | 0.20 | 0.05 | 0.0075 | 0.20 | 0.10 | 1.3 | 0.05 |
| Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.2% Offset (ksi) |
Elongation (%) |
Rockwell B scale |
|---|---|---|---|---|---|---|
| * Measured at room temperature, 68°F (20°C). | ||||||
| As Sand Cast | As Sand Cast | M01 |
43.5 Min 56.6 Typ |
14.5 Min 21.8 Typ |
15 Typ |
60 Typ |
| Rod, Bar, Wire and Forgings | As Hot Extruded | M30 |
61 Min 75 Typ |
34 Typ |
10 Typ |
75 Typ |
| Melting Point - Liquidus°F | 1616 |
|---|---|
| Melting Point - Solidus°F | 1589 |
| Densitylb/cu in. at 68°F | 0.3 |
| Specific Gravity | 8.3 |
| Electrical Conductivity% IACS at 68°F | 16.5 |
| Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 43 |
| Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 10 |
| Modulus of Rigidityksi | 5500 |
| Poisson's Ratio | 0.33 |
| Technique | Suitability |
|---|---|
| Soldering | Excellent |
| Brazing | Good |
| Oxyacetylene Welding | Good |
| Gas Shielded Arc Welding | Good |
| Coated Metal Arc Welding | Good |
| Spot Weld | Good |
| Seam Weld | Good |
| Butt Weld | Good |
| Capacity for Being Cold Worked | Poor |
| Capacity for Being Hot Formed | Excellent |
| Forgeability Rating | 120 |
| Machinability Rating | 80 |
Common Fabrication Processes
No fabrication process properties for this alloy
Thermal Properties
No thermal properties for this alloy
| Product Category | Product | Reason Category | Reason |
|---|---|---|---|
| Automotive | Connectors | ||
| Industrial | Fittings | ||
| Plumbing | Plumbing Fittings |
Applicable Specifications
No applicable specifications for this alloy
Corrosion Properties
No Corrosion Properties Available.