C69400
| Elements | |||||
|---|---|---|---|---|---|
| Cu(1,2) | Pb | Zn | Fe | Si | |
|
(1) Cu + Sum of Named Elements 99.5% min. (2) Cu value includes Ag. |
|||||
| Min (%) | 80.0 | 3.5 | |||
| Max (%) | 83.0 | 0.30 | Rem | 0.20 | 4.5 |
| Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.5% Ext (ksi) |
Elongation (%) |
Rockwell B scale | Section Size (in) |
|---|---|---|---|---|---|---|---|
| * Measured at room temperature, 68°F (20°C). | |||||||
| Rod | 1/8 Hard | H00 |
100 Typ |
57 Typ |
21 Typ |
0.75 | |
| 1/8 Hard | H00 |
100 Typ |
57 Typ |
21 Typ |
95 Typ |
0.75 | |
| Soft Anneal | O60 |
85 Typ |
43 Typ |
25 Typ |
1 | ||
| Soft Anneal | O60 |
77 Typ |
40 Typ |
25 Typ |
2 | ||
| Soft Anneal | O60 |
90 Typ |
45 Typ |
20 Typ |
0.5 | ||
| Soft Anneal | O60 |
90 Typ |
45 Typ |
20 Typ |
85 Typ |
0.5 | |
| Soft Anneal | O60 |
80 Typ |
40 Typ |
25 Typ |
85 Typ |
2 | |
| Soft Anneal | O60 |
85 Typ |
43 Typ |
25 Typ |
85 Typ |
1 | |
| Melting Point - Liquidus°F | 1685 |
|---|---|
| Melting Point - Solidus°F | 1510 |
| Densitylb/cu in. at 68°F | 0.296 |
| Specific Gravity | 8.19 |
| Electrical Conductivity% IACS at 68°F | 6.2 |
| Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 15 |
| Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 11.2 |
| Specific Heat CapacityBtu/ lb /°F at 68°F | 0.09 |
| Modulus of Elasticity in Tensionksi | 16000 |
| Technique | Suitability |
|---|---|
| Soldering | Excellent |
| Brazing | Excellent |
| Oxyacetylene Welding | Good |
| Spot Weld | Good |
| Seam Weld | Good |
| Butt Weld | Good |
| Capacity for Being Cold Worked | Poor |
| Capacity for Being Hot Formed | Excellent |
| Forgeability Rating | 80 |
| Machinability Rating | 30 |
Common Fabrication Processes
- Forging
- Screw Machining
| Treatment | Minimum* | Maximum* | ||
|---|---|---|---|---|
| * Temperature is measured in Fahrenheit. | ||||
| Annealing | 800 | 1200 | ||
| Hot Working Temperature | 1200 | 1600 | ||
| Product Category | Product | Reason Category | Reason |
|---|---|---|---|
| Industrial | Valve Stems | Corrosion Resistance | Corrosion Resistance |
| Valve Stems | Corrosion Resistance | Dezincification Resistance | |
| Valve Stems | Mechanical Properties | High Strength |
| Form | Specific Sub-Form | Application | System | Standard | Description |
|---|---|---|---|---|---|
| Rod | ASTM | B371/B371M | COPPER-ZINC-SILICON ALLOY ROD |