C69410
| Elements | |||||
|---|---|---|---|---|---|
| Cu(1) | Pb | Zn | Fe | Si | |
|
(1) Cu + Sum of Named Elements 99.5% min. |
|||||
| Min (%) | 81 | 11.0 | 3.5 | ||
| Max (%) | 0.09 | 15.0 | 0.20 | 4.5 | |
| Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.5% Ext (ksi) |
Elongation (%) |
Rockwell B scale | Section Size (in) |
|---|---|---|---|---|---|---|---|
| * Measured at room temperature, 68°F (20°C). | |||||||
| Forgings | 1/8 Hard | H00 |
100 Typ |
57 Typ |
21 Typ |
95 Typ |
0.75 |
| Rod | Soft Anneal | O60 |
80 Typ |
40 Typ |
25 Typ |
85 Typ |
2.0 |
| Soft Anneal | O60 |
85 Typ |
43 Typ |
25 Typ |
85 Typ |
1.0 | |
| Soft Anneal | O60 |
90 Typ |
45 Typ |
20 Typ |
85 Typ |
0.5 | |
| Melting Point - Liquidus°F | 1685 |
|---|---|
| Melting Point - Solidus°F | 1510 |
| Densitylb/cu in. at 68°F | 0.296 |
| Specific Gravity | 8.19 |
| Electrical Conductivity% IACS at 68°F | 6.2 |
| Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 15 |
| Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 11.2 |
| Modulus of Elasticity in Tensionksi | 16000 |
| Technique | Suitability |
|---|---|
| Soldering | Excellent |
| Brazing | Excellent |
| Oxyacetylene Welding | Good |
| Gas Shielded Arc Welding | Good |
| Coated Metal Arc Welding | Good |
| Spot Weld | Good |
| Seam Weld | Good |
| Butt Weld | Good |
| Capacity for Being Cold Worked | Poor |
| Capacity for Being Hot Formed | Excellent |
| Forgeability Rating | 80 |
| Machinability Rating | 30 |
Common Fabrication Processes
No fabrication process properties for this alloy
Thermal Properties
No thermal properties for this alloy
| Product Category | Product | Reason Category | Reason |
|---|---|---|---|
| Plumbing | Lead-free,dezincification resistant alloy for potable water components | ||
| Low Lead Valves and Fittings |
Applicable Specifications
No applicable specifications for this alloy
Corrosion Properties
No Corrosion Properties Available.