C70275
Elements | ||||||||||
---|---|---|---|---|---|---|---|---|---|---|
Cu(1,2) | Pb | Sn | Zn | Fe | Ni | Ca | Cr | Mg | Si | |
(1) Cu value includes Ag. (2) Cu + Sum of Named Elements 99.5% min. |
||||||||||
Min (%) | 0.30 | 0.30 | 0.50 | 0.002 | 0.10 | |||||
Max (%) | Rem | 0.01 | 1.0 | 1.0 | 0.25 | 1.5 | 0.01 | 0.06 | 0.20 | 0.50 |
Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.2% Offset (ksi) |
Elongation (%) |
Vickers Hardness, 500 gm |
---|---|---|---|---|---|---|
* Measured at room temperature, 68°F (20°C). | ||||||
Flat Products | 1/2 Hard and Stress Relieved | HR02 |
58 Min 73 Max |
54 Min 69 Max |
9 Min |
130 Min 150 Max |
Cold-worked (drawn), Stress-relieved Tempers, HR | HR |
76 Min 91 Max |
73 Min 87 Max |
3 Min |
150 Min 180 Max |
|
Hard and Stress Relieved | HR04 |
69 Min 83 Max |
65 Min 80 Max |
7 Min |
140 Min 170 Max |
Melting Point - Liquidus°F | 1985 |
---|---|
Melting Point - Solidus°F | 1920 |
Densitylb/cu in. at 68°F | 0.323 |
Specific Gravity | 8.94 |
Electrical Conductivity% IACS at 68°F | 33 |
Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 84.1 |
Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 9.5 |
Specific Heat CapacityBtu/ lb /°F at 68°F | 0.09 |
Modulus of Elasticity in Tensionksi | 18900 |
Technique | Suitability |
---|---|
Soldering | Excellent |
Brazing | Excellent |
Oxyacetylene Welding | Fair |
Gas Shielded Arc Welding | Fair |
Coated Metal Arc Welding | Fair |
Spot Weld | Good |
Seam Weld | Fair |
Capacity for Being Cold Worked | Good |
Capacity for Being Hot Formed | Good |
Forgeability Rating | 70 |
Machinability Rating | 20 |
Common Fabrication Processes
Treatment | Minimum* | Maximum* | ||
---|---|---|---|---|
* Temperature is measured in Fahrenheit. | ||||
Annealing | 660 | 1200 | ||
Hot Working Temperature | 1557 | 1755 |
Typical Uses
Applicable Specifications
Corrosion Properties