C71500
Elements | ||||||
---|---|---|---|---|---|---|
Cu(1,2) | Pb | Zn | Fe | Ni(3) | Mn | |
(1) Cu + Sum of Named Elements 99.5% min. (2) Cu value includes Ag. (3) Ni value includes Co. |
||||||
Min (%) | 0.40 | 29.0 | ||||
Max (%) | Rem | 0.05 | 1.0 | 1.0 | 33.0 | 1.0 |
Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.5% Ext (ksi) |
Elongation (%) |
Rockwell B scale | Rockwell F scale | Section Size (in) |
Cold Work (%) |
---|---|---|---|---|---|---|---|---|---|
* Measured at room temperature, 68°F (20°C). | |||||||||
Flat Products | As Hot Rolled | M20 |
55 Typ |
45 Typ |
35 Typ |
1 | |||
Rod | 1/2 Hard | H02 |
75 Typ |
15 Typ |
80 Typ |
1 | 20 | ||
Tube | Nominal Grain Size 0.025 mm | OS025 |
60 Typ |
45 Typ |
45 Typ |
80 Typ |
|||
Nominal Grain Size 0.035 mm | OS035 |
54 Typ |
45 Typ |
36 Typ |
77 Typ |
Melting Point - Liquidus°F | 2260 |
---|---|
Melting Point - Solidus°F | 2140 |
Densitylb/cu in. at 68°F | 0.323 |
Specific Gravity | 8.94 |
Electrical Conductivity% IACS at 68°F | 4.6 |
Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 17 |
Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 9 |
Specific Heat CapacityBtu/ lb /°F at 68°F | 0.09 |
Modulus of Elasticity in Tensionksi | 22000 |
Modulus of Rigidityksi | 8300 |
Technique | Suitability |
---|---|
Soldering | Excellent |
Brazing | Excellent |
Oxyacetylene Welding | Good |
Gas Shielded Arc Welding | Excellent |
Coated Metal Arc Welding | Excellent |
Spot Weld | Excellent |
Seam Weld | Excellent |
Butt Weld | Excellent |
Capacity for Being Cold Worked | Good |
Capacity for Being Hot Formed | Good |
Machinability Rating | 20 |
Common Fabrication Processes
- Forming and Bending
- Welding
Treatment | Minimum* | Maximum* | ||
---|---|---|---|---|
* Temperature is measured in Fahrenheit. | ||||
Annealing | 1200 | 1500 | ||
Hot Working Temperature | 1700 | 1900 |
Product Category | Product | Reason Category | Reason |
---|---|---|---|
Industrial | Boiler Parts | Conductivity (Thermal) | Thermal Conductivity |
Boiler Parts | Corrosion Resistance | Corrosion Resistance to 700 F. | |
Boiler Parts | Welding Characteristics | Weldability | |
Condenser Components | Corrosion Resistance | Corrosion Resistance | |
Condenser Components | Corrosion Resistance | Corrosion Resistance to 700 F. | |
Condenser Components | Forming Characteristics | Formability | |
Condenser Components | Mechanical Properties | Moderate Strength | |
Condenser Plates | Corrosion Resistance | Corrosion Resistance | |
Condenser Plates | Corrosion Resistance | Corrosion Resistance to 700 F. | |
Condenser Plates | Corrosion Resistance | Corrosion Resistance to Salt Water | |
Condenser Plates | Forming Characteristics | Formability | |
Condenser Plates | Mechanical Properties | Moderate Strength | |
Condensers | Corrosion Resistance | Corrosion Resistance | |
Condensers | Corrosion Resistance | Corrosion Resistance to 700 F. | |
Condensers | Corrosion Resistance | Corrosion Resistance to Salt Water | |
Condensers | Mechanical Properties | Moderate Strength | |
Distiller Tubes | Corrosion Resistance | Corrosion Resistance | |
Distiller Tubes | Corrosion Resistance | Corrosion Resistance to 700 F. | |
Distiller Tubes | Corrosion Resistance | Corrosion Resistance to Salt Water | |
Distiller Tubes | Forming Characteristics | Formability | |
Distiller Tubes | Mechanical Properties | Moderate Strength | |
Distiller Tubes | Welding Characteristics | Weldability | |
Evaporator Tubes | Corrosion Resistance | Corrosion Resistance | |
Evaporator Tubes | Corrosion Resistance | Corrosion Resistance to 700 F. | |
Evaporator Tubes | Corrosion Resistance | Corrosion Resistance to Salt Water | |
Evaporator Tubes | Forming Characteristics | Formability | |
Evaporator Tubes | Mechanical Properties | Moderate Strength | |
Evaporator Tubes | Welding Characteristics | Weldability | |
Ferrules | Corrosion Resistance | Corrosion Resistance | |
Ferrules | Corrosion Resistance | Corrosion Resistance to 700 F. | |
Ferrules | Corrosion Resistance | Corrosion Resistance to Salt Water | |
Ferrules | Forming Characteristics | Formability | |
Ferrules | Mechanical Properties | Moderate Strength | |
Flexible Metal Hose | Corrosion Resistance | Corrosion Resistance | |
Flexible Metal Hose | Corrosion Resistance | Corrosion Resistance to Salt Water | |
Flexible Metal Hose | Forming Characteristics | Formability | |
Heat Exchanger Components | Corrosion Resistance | Corrosion Resistance | |
Heat Exchanger Components | Corrosion Resistance | Corrosion Resistance to 700 F. | |
Heat Exchanger Components | Corrosion Resistance | Corrosion Resistance to Salt Water | |
Heat Exchanger Components | Forming Characteristics | Formability | |
Heat Exchanger Components | Mechanical Properties | Moderate Strength | |
Heat Exchanger Tubes | Corrosion Resistance | Corrosion Resistance | |
Heat Exchanger Tubes | Corrosion Resistance | Corrosion Resistance to 700 F. | |
Heat Exchanger Tubes | Corrosion Resistance | Corrosion Resistance to Salt Water | |
Heat Exchanger Tubes | Forming Characteristics | Formability | |
Heat Exchanger Tubes | Mechanical Properties | Moderate Strength | |
Heat Exchanger Tubes | Welding Characteristics | Weldability | |
Process Equipment | Corrosion Resistance | Corrosion Resistance | |
Process Equipment | Corrosion Resistance | Corrosion Resistance to 700 F. | |
Process Equipment | Forming Characteristics | Formability | |
Process Equipment | Mechanical Properties | Moderate Strength | |
Propeller Sleeves | Corrosion Resistance | Corrosion Resistance | |
Propeller Sleeves | Corrosion Resistance | Corrosion Resistance to 700 F. | |
Propeller Sleeves | Forming Characteristics | Formability | |
Propeller Sleeves | Mechanical Properties | Moderate Strength | |
Pump Impellers | Corrosion Resistance | Corrosion Resistance to 700 F. | |
Pump Impellers | Corrosion Resistance | Corrosion Resistance to Salt Water | |
Pump Impellers | Welding Characteristics | Weldability | |
Refrigerators | Corrosion Resistance | Corrosion Resistance | |
Refrigerators | Corrosion Resistance | Corrosion Resistance to 700 F. | |
Refrigerators | Mechanical Properties | Moderate Strength | |
Weld Wire | Welding Characteristics | Weldability | |
Welding Backing Rings | Corrosion Resistance | Corrosion Resistance | |
Welding Backing Rings | Welding Characteristics | Weldability | |
Marine | Fittings | Corrosion Resistance | Corrosion Resistance |
Fittings | Corrosion Resistance | Corrosion Resistance to 700 F. | |
Fittings | Corrosion Resistance | Corrosion Resistance to Salt Water | |
Fittings | Forming Characteristics | Formability | |
Fittings | Fouling Resistance | Non-Fouling | |
Fittings | Mechanical Properties | Moderate Strength | |
Pump Bodies and Internal Parts-Sea Water | Corrosion Resistance | Corrosion Resistance | |
Pump Bodies and Internal Parts-Sea Water | Corrosion Resistance | Corrosion Resistance to Salt Water | |
Pump Bodies and Internal Parts-Sea Water | Forming Characteristics | Cold Workability | |
Pump Bodies and Internal Parts-Sea Water | Forming Characteristics | Hot Workable | |
Pump Bodies and Internal Parts-Sea Water | Mechanical Properties | Moderate Strength | |
Pump Bodies and Internal Parts-Sea Water | Welding Characteristics | Weldability | |
Salt Water Flanges | Corrosion Resistance | Corrosion Resistance | |
Salt Water Flanges | Corrosion Resistance | Corrosion Resistance to Salt Water | |
Salt Water Flanges | Welding Characteristics | Weldability | |
Salt Water Pipe Fittings | Corrosion Resistance | Corrosion Resistance | |
Salt Water Pipe Fittings | Corrosion Resistance | Corrosion Resistance to Salt Water | |
Salt Water Pipe Fittings | Welding Characteristics | Weldability | |
Salt Water Piping | Corrosion Resistance | Corrosion Resistance | |
Salt Water Piping | Corrosion Resistance | Corrosion Resistance to Salt Water | |
Salt Water Piping | Welding Characteristics | Weldability | |
Sea Water Condensers | Corrosion Resistance | Corrosion Resistance | |
Sea Water Condensers | Corrosion Resistance | Corrosion Resistance to 700 F. | |
Sea Water Condensers | Corrosion Resistance | Corrosion Resistance to Salt Water | |
Sea Water Condensers | Fouling Resistance | Non-Fouling | |
Sea Water Condensers | Mechanical Properties | Moderate Strength | |
Valve Bodies, Sea Water Service | Corrosion Resistance | Corrosion Resistance | |
Valve Bodies, Sea Water Service | Corrosion Resistance | Corrosion Resistance to Salt Water | |
Valve Bodies, Sea Water Service | Forming Characteristics | Cold Workability | |
Valve Bodies, Sea Water Service | Forming Characteristics | Hot Workable | |
Valve Bodies, Sea Water Service | Welding Characteristics | Weldability | |
Water Boxes - Salt Water Applications | Corrosion Resistance | Corrosion Resistance | |
Water Boxes - Salt Water Applications | Corrosion Resistance | Corrosion Resistance to Salt Water | |
Water Boxes - Salt Water Applications | Welding Characteristics | Weldability |
Form | Specific Sub-Form | Application | System | Standard | Description |
---|---|---|---|---|---|
Bar | SAE | J461 | WROUGHT AND CAST COPPER ALLOYS | ||
ASTM | B122/B122M | COPPER-NICKEL-ZINC ALLOY (NICKEL-SILVER) AND COPPER-NICKEL PLATE, SHEET, STRIP, AND ROLLED BAR | |||
MILITARY | MIL-C-15726 | COPPER-NICKEL ALLOY ROD, FLAT PRODUCTS (FLAT WIRE, STRIP, SHEET, BAR, AND PLATE) AND FORGINGS | |||
SAE | J463 | WROUGHT COPPER AND COPPER ALLOYS | |||
Bolts | ASTM | F468 | NONFERROUS BOLTS, HEX CAP SCREWS, AND STUDS FOR GENERAL USE | ||
Condenser & Heat Exchanger Tube with Integral Fins | ASTM | B956/B956M | WELDED COPPER AND COPPER-ALLOY CONDENSER AND HEAT EXCHANGER TUBES WITH INTEGRAL FINS | ||
Electrode | Welding | AWS | A5.6 | COPPER AND COPPER ALLOY COVERED ELECTRODES | |
Welding | MILITARY | MIL-E-22200/4 | ELECTRODES, WELDING, COVERED, COPPER-NICKEL ALLOY | ||
Nuts | ASTM | F467 | NONFERROUS NUTS FOR GENERAL USE | ||
Pipe | ASTM | B466/B466M | SEAMLESS COPPER-NICKEL PIPE AND TUBE | ||
ASME | SB467 | WELDED COPPER-NICKEL PIPE | |||
ASTM | B467 | WELDED COPPER-NICKEL PIPE | |||
Pipe and Tube | ASME | SB466 | SEAMLESS COPPER-NICKEL PIPE AND TUBE | ||
Plate | Condenser Tube | ASME | SB171 | COPPER ALLOY CONDENSER TUBE PLATES | |
ASTM | B122/B122M | COPPER-NICKEL-ZINC ALLOY (NICKEL-SILVER) AND COPPER-NICKEL PLATE, SHEET, STRIP, AND ROLLED BAR | |||
Condenser Tube | SAE | J461 | WROUGHT AND CAST COPPER ALLOYS | ||
SAE | J463 | WROUGHT COPPER AND COPPER ALLOYS | |||
SAE | J461 | WROUGHT AND CAST COPPER ALLOYS | |||
Condenser Tube | SAE | J463 | WROUGHT COPPER AND COPPER ALLOYS | ||
MILITARY | MIL-C-15726 | COPPER-NICKEL ALLOY ROD, FLAT PRODUCTS (FLAT WIRE, STRIP, SHEET, BAR, AND PLATE) AND FORGINGS | |||
Condenser Tube | ASTM | B171/B171M | COPPER ALLOY CONDENSER TUBE PLATES | ||
ASTM | B432 | COPPER AND COPPER ALLOY CLAD STEEL PLATE | |||
Rod | MILITARY | MIL-C-15726 | COPPER-NICKEL ALLOY ROD, FLAT PRODUCTS (FLAT WIRE, STRIP, SHEET, BAR, AND PLATE) AND FORGINGS | ||
Rod & Bar | ASTM | B151/B151M | COPPER-NICKEL-ZINC ALLOY (NICKEL-SILVER) AND COPPER-NICKEL ROD AND BAR | ||
Screws | ASTM | F468 | NONFERROUS BOLTS, HEX CAP SCREWS, AND STUDS FOR GENERAL USE | ||
Sheet | ASTM | B122/B122M | COPPER-NICKEL-ZINC ALLOY (NICKEL-SILVER) AND COPPER-NICKEL PLATE, SHEET, STRIP, AND ROLLED BAR | ||
SAE | J461 | WROUGHT AND CAST COPPER ALLOYS | |||
SAE | J463 | WROUGHT COPPER AND COPPER ALLOYS | |||
MILITARY | MIL-C-15726 | COPPER-NICKEL ALLOY ROD, FLAT PRODUCTS (FLAT WIRE, STRIP, SHEET, BAR, AND PLATE) AND FORGINGS | |||
Strip | SAE | J461 | WROUGHT AND CAST COPPER ALLOYS | ||
ASTM | B122/B122M | COPPER-NICKEL-ZINC ALLOY (NICKEL-SILVER) AND COPPER-NICKEL PLATE, SHEET, STRIP, AND ROLLED BAR | |||
SAE | J463 | WROUGHT COPPER AND COPPER ALLOYS | |||
MILITARY | MIL-C-15726 | COPPER-NICKEL ALLOY ROD, FLAT PRODUCTS (FLAT WIRE, STRIP, SHEET, BAR, AND PLATE) AND FORGINGS | |||
Studs | ASTM | F468 | NONFERROUS BOLTS, HEX CAP SCREWS, AND STUDS FOR GENERAL USE | ||
Tube | MILITARY | MIL-T-16420 | TUBE, COPPER-NICKEL ALLOY, SEAMLESS AND WELDED | ||
ASTM | B395/B395M | U-BEND SEAMLESS COPPER AND COPPER ALLOY HEAT EXCHANGER AND CONDENSER TUBES | |||
Condenser Tube | ASME | SB111 | COPPER AND COPPER ALLOY SEAMLESS CONDENSER TUBES & FERRULE STOCK | ||
ASTM | B359/B359M | COPPER AND COPPER-ALLOY SEAMLESS CONDENSER AND HEAT EXCHANGER TUBES WITH INTEGRAL FINS | |||
Condenser Tube | MILITARY | MIL-T-15005 | TUBES, COPPER-NICKEL ALLOY CONDENSER AND HEAT EXCHANGER | ||
ASME | SB395 | U-BEND SEAMLESS COPPER & COPPER ALLOY HEAT EXCHANGER & CONDENSER TUBE | |||
ASME | SB543 | WELDED COPPER AND COPPER ALLOY TUBE | |||
Condenser Tube | ASTM | B111/B111M | COPPER AND COPPER ALLOY SEAMLESS CONDENSER TUBES AND FERRULE STOCK | ||
ASME | SB359 | COPPER & COPPER ALLOY SEAMLESS CONDENSER & HEAT EXCHANGER TUBES WITH INTEGRAL FINS | |||
MILITARY | MIL-T-22214 | TUBE, CONDENSER AND HEAT EXCHANGER WITH INTEGRAL FINS | |||
Condenser Tube | SAE | J461 | WROUGHT AND CAST COPPER ALLOYS | ||
Condenser Tube | SAE | J463 | WROUGHT COPPER AND COPPER ALLOYS | ||
ASTM | B466/B466M | SEAMLESS COPPER-NICKEL PIPE AND TUBE | |||
ASTM | B543/B543M | WELDED COPPER AND COPPER ALLOY HEAT EXCHANGER TUBE | |||
Condenser Tube | ASTM | B552 | SEAMLESS AND WELDED COPPER-NICKEL TUBES FOR WATER DESALTING PLANTS | ||
Wire | MILITARY | MIL-C-15726 | COPPER-NICKEL ALLOY ROD, FLAT PRODUCTS (FLAT WIRE, STRIP, SHEET, BAR, AND PLATE) AND FORGINGS |
Corrosion Properties