C71950
| Elements | |||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Cu(1) | Pb | Fe | P | Ni | B | Bi | C | Co | Cr | Mn | S | Si | Ti | Zr | |
|
(1) Cu + Sum of Named Elements 99.93% min. |
|||||||||||||||
| Min (%) | 0.5 | 29.0 | 1.6 | 0.5 | 0.20 | 0.03 | 0.05 | ||||||||
| Max (%) | Rem | 0.005 | 1.0 | 0.005 | 32.0 | 0.001 | 0.001 | 0.020 | 0.050 | 2.0 | 1.0 | 0.005 | 0.40 | 0.15 | 0.15 |
| Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.2% Offset (ksi) |
Elongation (%) |
Brinell Hardness, 3000 kg load | Shear Strength (ksi) |
Impact Strength (ft-lbs) |
|---|---|---|---|---|---|---|---|---|
| * Measured at room temperature, 68°F (20°C). | ||||||||
| Rod, Bar & Forging | Spinodal Hardened-Low Strength (ATLS) | TX00 |
80 Min 87 Typ 119 Max |
51 Min 61 Typ 105 Max |
20 Min 27 Max |
170 Min 250 Max |
39 Typ |
81.13 Typ |
| Melting Point - Liquidus°F | 2204 |
|---|---|
| Melting Point - Solidus°F | 2120 |
| Densitylb/cu in. at 68°F | 0.318 |
| Specific Gravity | 8.8 |
| Electrical Conductivity% IACS at 68°F | 4 |
| Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 13.3 |
| Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 10 |
| Modulus of Elasticity in Tensionksi | 20200 |
| Modulus of Rigidityksi | 782 |
| Magnetic Permeability | 1.01 |
| Poisson's Ratio | 0.3 |
Fabrication Properties
No fabrication properties for this alloy
Common Fabrication Processes
No fabrication process properties for this alloy
Thermal Properties
No thermal properties for this alloy
Typical Uses
No information for this alloy
Applicable Specifications
No applicable specifications for this alloy
Corrosion Properties
No Corrosion Properties Available.