Find suppliers for this alloy
C72670
Elements | |||||||||
---|---|---|---|---|---|---|---|---|---|
Cu(1) | Pb | Sn | Zn | Fe | Ni | Mg | Mn | Te | |
(1) Cu + Sum of Named Elements 99.5% min. |
|||||||||
Min (%) | 4.5 | 7.0 | 0.05 | 0.20 | |||||
Max (%) | Rem | 0.10 | 5.5 | 0.50 | 0.50 | 8.0 | 0.15 | 0.30 | 0.30 |
Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.2% Offset (ksi) |
Elongation (%) |
---|---|---|---|---|---|
* Measured at room temperature, 68°F (20°C). | |||||
Rod & Bar | Solution Heat Treated and Cold Worked: 1/4 Hard | TD01 |
66.7 Min 72.5 Max |
53.7 Min 69.6 Max |
7.0 Max |
1/4 Hard and Precipitation Heat Treated | TH01 |
116.0 Min 123.3 Max |
94.1 Min 110.2 Max |
10.0 Max | |
Hard and Precipitation Heat Treateed (HT) | TH04 |
134.2 Min 143.6 Max |
129.1 Min 136.3 Max |
5.0 Max | |
Wire | Solution Heat Treated and Cold Worked: 1/4 Hard | TD01 |
66.7 Min 72.5 Max |
53.7 Min 69.6 Max |
7.0 Min 30.0 Max |
Solution Heat Treated and Cold Worked: Hard | TD04 |
98.6 Min 107.3 Max |
88.5 Min 95.7 Max |
4.0 Max |
Melting Point - Liquidus°F | 1759 |
---|---|
Densitylb/cu in. at 68°F | .318 |
Specific Gravity | 8.8 |
Electrical Conductivity% IACS at 68°F | 13 |
Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 9.9 |
Modulus of Elasticity in Tensionksi | 16700 |
Technique | Suitability |
---|---|
Capacity for Being Cold Worked | Good |
Capacity for Being Hot Formed | Excellent |
Common Fabrication Processes
Typical Uses
Applicable Specifications
Corrosion Properties