C77000
Elements | ||||||
---|---|---|---|---|---|---|
Cu(1,2) | Pb | Zn | Fe | Ni(3) | Mn | |
(1) Cu + Sum of Named Elements 99.5% min. (2) Cu value includes Ag. (3) Ni value includes Co. |
||||||
Min (%) | 53.5 | 16.5 | ||||
Max (%) | 56.5 | 0.05 | Rem | 0.25 | 19.5 | 0.50 |
Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.5% Ext (ksi) |
Elongation (%) |
Rockwell B scale | Rockwell F scale | Rockwell 30T scale | Torsion Modulus (ksi) |
Section Size (in) |
Cold Work (%) |
---|---|---|---|---|---|---|---|---|---|---|---|
* Measured at room temperature, 68°F (20°C). | |||||||||||
Flat Products | Extra Hard | H06 |
108 Typ |
90 Typ |
2.5 Typ |
96 Typ |
80 Typ |
0.04 | |||
Hard | H04 |
100 Typ |
85 Typ |
3 Typ |
91 Typ |
77 Typ |
6.8 Typ | 0.04 | |||
Nominal Grain Size 0.035 mm | OS035 |
60 Typ |
27 Typ |
40 Typ |
55 Typ |
90 Typ |
0.04 | ||||
Spring | H08 |
115 Typ |
2.5 Typ |
99 Typ |
81 Typ |
0.04 | |||||
Wire | Hard | H04 |
145 Typ |
2 Typ |
0.08 | 68 | |||||
Nominal Grain Size 0.035 mm | OS035 |
60 Typ |
40 Typ |
0.08 |
Melting Point - Liquidus°F | 1930 |
---|---|
Densitylb/cu in. at 68°F | 0.314 |
Specific Gravity | 8.7 |
Electrical Conductivity% IACS at 68°F | 5.5 |
Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 17 |
Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 9.3 |
Specific Heat CapacityBtu/ lb /°F at 68°F | 0.09 |
Modulus of Elasticity in Tensionksi | 18000 |
Modulus of Rigidityksi | 6800 |
Technique | Suitability |
---|---|
Soldering | Excellent |
Brazing | Excellent |
Oxyacetylene Welding | Good |
Gas Shielded Arc Welding | Fair |
Coated Metal Arc Welding | Not Recommended |
Spot Weld | Good |
Seam Weld | Fair |
Butt Weld | Good |
Capacity for Being Cold Worked | Good |
Capacity for Being Hot Formed | Poor |
Machinability Rating | 30 |
Common Fabrication Processes
Treatment | Minimum* | Maximum* | ||
---|---|---|---|---|
* Temperature is measured in Fahrenheit. | ||||
Annealing | 1100 | 1500 |
Product Category | Product | Reason Category | Reason |
---|---|---|---|
Electrical | Resistance Wire | Conductivity (Electrical) | Low Conductivity |
Springs | Conductivity (Thermal) | Thermal Conductivity | |
Springs | Corrosion Resistance | Corrosion Resistance | |
Springs | Mechanical Properties | High Strength | |
Springs | Thermal Properties | Resistance to Stress Relaxation | |
Industrial | Optical Goods | Appearance | Appearance |
Optical Goods | Corrosion Resistance | Corrosion Resistance | |
Optical Goods | Mechanical Properties | Moderate Strength |
Form | Specific Sub-Form | Application | System | Standard | Description |
---|---|---|---|---|---|
Bar | SAE | J463 | WROUGHT COPPER AND COPPER ALLOYS | ||
SAE | J461 | WROUGHT AND CAST COPPER ALLOYS | |||
ASTM | B151/B151M | COPPER-NICKEL-ZINC ALLOY (NICKEL-SILVER) AND COPPER-NICKEL ROD AND BAR | |||
ASTM | B122/B122M | COPPER-NICKEL-ZINC ALLOY (NICKEL-SILVER) AND COPPER-NICKEL PLATE, SHEET, STRIP, AND ROLLED BAR | |||
Plate | ASTM | B122/B122M | COPPER-NICKEL-ZINC ALLOY (NICKEL-SILVER) AND COPPER-NICKEL PLATE, SHEET, STRIP, AND ROLLED BAR | ||
Rod | SAE | J461 | WROUGHT AND CAST COPPER ALLOYS | ||
SAE | J463 | WROUGHT COPPER AND COPPER ALLOYS | |||
ASTM | B151/B151M | COPPER-NICKEL-ZINC ALLOY (NICKEL-SILVER) AND COPPER-NICKEL ROD AND BAR | |||
Sheet | SAE | J461 | WROUGHT AND CAST COPPER ALLOYS | ||
SAE | J463 | WROUGHT COPPER AND COPPER ALLOYS | |||
ASTM | B122/B122M | COPPER-NICKEL-ZINC ALLOY (NICKEL-SILVER) AND COPPER-NICKEL PLATE, SHEET, STRIP, AND ROLLED BAR | |||
Strip | SAE | J463 | WROUGHT COPPER AND COPPER ALLOYS | ||
SAE | J461 | WROUGHT AND CAST COPPER ALLOYS | |||
ASTM | B122/B122M | COPPER-NICKEL-ZINC ALLOY (NICKEL-SILVER) AND COPPER-NICKEL PLATE, SHEET, STRIP, AND ROLLED BAR | |||
Wire | ASTM | B206/B206M | COPPER-NICKEL-ZINC ALLOY (NICKEL-SILVER WIRE) AND COPPER-NICKEL ALLOY WIRE |
Corrosion Properties