C79350
Elements | |||||||
---|---|---|---|---|---|---|---|
Cu(1,2) | Pb | Sn | Zn | Fe | Ni(3) | Mn | |
(1) Cu + Sum of Named Elements 99.5% min. (2) Cu value includes Ag. (3) Ni value includes Co. |
|||||||
Min (%) | 59.0 | 0.8 | 23.0 | ||||
Max (%) | 63.0 | 1.1 | 0.6 | Rem | 0.25 | 26.0 | 0.50 |
Form | Temper | Temper Code | Tensile Strength (ksi) |
Elongation (%) |
---|---|---|---|---|
* Measured at room temperature, 68°F (20°C). | ||||
Rod | Hard | H04 |
80 Min 87 Typ |
2 Min |
Hard | H04 |
80 Min 87 Typ |
2 Min |
|
Hard | H04 |
87 Min 98 Typ |
2 Min |
|
Wire | Hard | H04 |
80 Min 87 Typ |
2 Min |
Hard | H04 |
87 Min 98 Typ |
2 Min |
|
Hard | H04 |
80 Min 87 Typ |
2 Min |
Melting Point - Liquidus°F | 2140 |
---|---|
Melting Point - Solidus°F | 2100 |
Densitylb/cu in. at 68°F | 0.318 |
Specific Gravity | 8.8 |
Electrical Conductivity% IACS at 68°F | 4 |
Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 12 |
Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 9.1 |
Specific Heat CapacityBtu/ lb /°F at 68°F | 0.095 |
Modulus of Elasticity in Tensionksi | 24200 |
Technique | Suitability |
---|---|
Soldering | Good |
Brazing | Good |
Oxyacetylene Welding | Not Recommended |
Gas Shielded Arc Welding | Not Recommended |
Coated Metal Arc Welding | Not Recommended |
Spot Weld | Not Recommended |
Seam Weld | Not Recommended |
Butt Weld | Not Recommended |
Capacity for Being Cold Worked | Good |
Capacity for Being Hot Formed | Not Recommended |
Machinability Rating | 60 |
Common Fabrication Processes
- Forming
- Machining
- Stamping
Treatment | Minimum* | Value* | Time** | |
---|---|---|---|---|
* Temperature is measured in Fahrenheit. ** Time is measured in minutes. | ||||
Stress Relief | 482 | |||
Solution Treatment | 1382 | 0 |
Product Category | Product | Reason Category | Reason |
---|---|---|---|
Industrial | Fasteners | Corrosion Resistance | Corrosion Resistance |
Fiber Optic Connectors | Magnetic Properties | Non-Magnetic |
Applicable Specifications
Corrosion Properties