C81300
Elements | |||
---|---|---|---|
Cu(1,2) | Be | Co | |
(1) Cu value includes Ag. (2) Cu + Sum of Named Elements 99.5% min. |
|||
Min (%) | 98.5 | 0.02 | 0.6 |
Max (%) | 0.10 | 1.0 |
Form | Temper | Temper Code | Brinell Hardness, 500 kg load |
---|---|---|---|
* Measured at room temperature, 68°F (20°C). | |||
As Sand Cast | As Sand Cast | M01 | 89 Typ |
Melting Point - Liquidus°F | 2000 |
---|---|
Melting Point - Solidus°F | 1950 |
Densitylb/cu in. at 68°F | 0.318 |
Specific Gravity | 8.81 |
Electrical Conductivity% IACS at 68°F | 60 |
Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 150 |
Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 10 |
Specific Heat CapacityBtu/ lb /°F at 68°F | 0.093 |
Modulus of Elasticity in Tensionksi | 16000 |
Casting Attribute | Level |
---|---|
Casting Yield | Low |
Drossing | Low |
Effect of Section Size | Low |
Fluidity | Medium |
Gassing | High |
Patternmakers Shrinkage inches per inch | 4/16 |
Shrinkage in Solidification | High |
Technique | Suitability |
---|---|
Soldering | Excellent |
Brazing | Good |
Oxyacetylene Welding | Not Recommended |
Gas Shielded Arc Welding | Fair |
Coated Metal Arc Welding | Fair |
Machinability Rating | 20 |
Common Fabrication Processes
Treatment | Minimum* | Maximum* | Value* | Time** | Medium |
---|---|---|---|---|---|
* Temperature is measured in Fahrenheit. ** Time is measured in minutes. | |||||
Stress Relief | 500 | ||||
Solution Treatment | 1800 | 1850 | 1 | Water | |
Precipitation Treatment | 900 | 2 | Air |
Typical Uses
Applicable Specifications
Corrosion Properties