C81400
Elements | |||
---|---|---|---|
Cu(1) | Be | Cr | |
(1) Cu + Sum of Named Elements 99.5% min. |
|||
Min (%) | 0.02 | 0.6 | |
Max (%) | Rem | 0.10 | 1.0 |
Form | Temper | Temper Code | Tensile Strength (ksi) |
Elongation (%) |
Rockwell B scale | Torsion Modulus (ksi) |
---|---|---|---|---|---|---|
* Measured at room temperature, 68°F (20°C). | ||||||
As Sand Cast | As Sand Cast | M01 |
45 Min for Standard |
15 Min for Standard |
||
Precipitation Hardened | TF00 |
53 Min for Standard |
11 Min for Standard |
69 Typ |
6 Typ |
Melting Point - Liquidus°F | 2000 |
---|---|
Melting Point - Solidus°F | 1950 |
Densitylb/cu in. at 68°F | 0.318 |
Specific Gravity | 8.81 |
Electrical Conductivity% IACS at 68°F | 60 |
Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 150 |
Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 10 |
Specific Heat CapacityBtu/ lb /°F at 68°F | 0.093 |
Modulus of Elasticity in Tensionksi | 16000 |
Shear Modulusksi | 5900 |
Casting Attribute | Level |
---|---|
Casting Yield | Medium |
Drossing | High |
Effect of Section Size | Low |
Fluidity | Medium |
Gassing | High |
Patternmakers Shrinkage inches per inch | 4/16 |
Shrinkage in Solidification | High |
Shrinkage During Freezing | High |
Technique | Suitability |
---|---|
Soldering | Excellent |
Brazing | Good |
Oxyacetylene Welding | Not Recommended |
Gas Shielded Arc Welding | Fair |
Coated Metal Arc Welding | Fair |
Machinability Rating | 20 |
Common Fabrication Processes
Treatment | Minimum* | Maximum* | Value* | Time** | Medium |
---|---|---|---|---|---|
* Temperature is measured in Fahrenheit. ** Time is measured in minutes. | |||||
Stress Relief | 500 | ||||
Solution Treatment | 1830 | 1850 | 0.5 | Water | |
Precipitation Treatment | 900 | 2 | Air |
Product Category | Product | Reason Category | Reason |
---|---|---|---|
Electrical | Electrical Parts | Conductivity (Electrical) | Electrical Conductivity |
Electrical Parts | Conductivity (Thermal) | Thermal Conductivity | |
Electrical Parts | Corrosion Resistance | Corrosion Resistance | |
Electrical Parts | Corrosion Resistance | Oxidation Resistance | |
Electrical Parts | Mechanical Properties | Moderate Strength | |
Higher Hardness Electrical Conductors | Conductivity (Electrical) | Electrical Conductivity | |
Higher Hardness Electrical Conductors | Conductivity (Thermal) | Thermal Conductivity | |
Higher Hardness Electrical Conductors | Corrosion Resistance | Corrosion Resistance | |
Higher Hardness Electrical Conductors | Corrosion Resistance | Oxidation Resistance | |
Higher Hardness Electrical Conductors | Mechanical Properties | Moderate Strength | |
Industrial | Higher Hardness Thermal Conductors | Conductivity (Electrical) | Electrical Conductivity |
Higher Hardness Thermal Conductors | Conductivity (Thermal) | Thermal Conductivity | |
Higher Hardness Thermal Conductors | Corrosion Resistance | Corrosion Resistance | |
Higher Hardness Thermal Conductors | Corrosion Resistance | Oxidation Resistance | |
Higher Hardness Thermal Conductors | Mechanical Properties | Moderate Strength |
Form | Specific Sub-Form | Application | System | Standard | Description |
---|---|---|---|---|---|
As Sand Cast | Castings | ASTM | B770 | COPPER-BERYLLIUM SAND CASTINGS | |
Ingot | ASTM | B30 | COPPER BASE ALLOYS IN INGOT FORM |
Corrosion Properties