C82510
Elements | |||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|
Cu(1) | Pb | Sn | Zn | Fe | Ni | Al | Be | Co | Cr | Si | |
(1) Cu + Sum of Named Elements 99.5% min. |
|||||||||||
Min (%) | 1.90 | 1.0 | 0.20 | ||||||||
Max (%) | Rem | 0.02 | 0.10 | 0.10 | 0.25 | 0.20 | 0.15 | 2.15 | 1.2 | 0.09 | 0.35 |
Form | Temper | Temper Code | Tensile Strength (ksi) |
Elongation (%) |
---|---|---|---|---|
* Measured at room temperature, 68°F (20°C). | ||||
As Sand Cast | Precipitation Hardened | TF00 |
160 Min for Standard |
1 Min for Standard |
Solution Heat Treated | TB00 |
80 Min for Standard |
10 Min for Standard |
Melting Point - Liquidus°F | 1800 |
---|---|
Melting Point - Solidus°F | 1575 |
Densitylb/cu in. at 68°F | 0.298 |
Specific Gravity | 8.26 |
Electrical Conductivity% IACS at 68°F | 20 |
Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 72.5 |
Coefficient of Thermal Expansion 68-39210 to -6 power per °F (68 – 392°F) | 8.6 |
Specific Heat CapacityBtu/ lb /°F at 68°F | 0.1 |
Modulus of Elasticity in Tensionksi | 18500 |
Change in Density During Aging% | 0.6 |
Magnetic Permeability | 1.002 |
Poisson's Ratio | 0.3 |
Casting Characteristics
Fabrication Properties
Common Fabrication Processes
Thermal Properties
Product Category | Product | Reason Category | Reason |
---|---|---|---|
Architecture | Sculpture | Appearance | Appearance |
Sculpture | Casting Characteristics | Castability | |
Sculpture | Corrosion Resistance | Corrosion Resistance | |
Sculpture | Mechanical Properties | Very High Strength | |
Consumer | Golf Clubs | Corrosion Resistance | Corrosion Resistance |
Golf Clubs | Mechanical Properties | High Modulus of Elasticity | |
Golf Clubs | Mechanical Properties | Very High Strength | |
Jewelry | Appearance | Appearance | |
Jewelry | Casting Characteristics | Castability | |
Jewelry | Corrosion Resistance | Corrosion Resistance | |
Jewelry | Mechanical Properties | Ductility | |
Jewelry | Mechanical Properties | Very High Strength | |
Safety Tools | Corrosion Resistance | Corrosion Resistance | |
Safety Tools | Mechanical Properties | Very High Strength | |
Safety Tools | Non-Magnetic | Non-Magnetic | |
Safety Tools | Non-Sparking | Non-Sparking | |
Industrial | Aluminum Die Cast Plunger Tips | Conductivity (Thermal) | Thermal Conductivity |
Aluminum Die Cast Plunger Tips | Corrosion Resistance | Corrosion Resistance | |
Aluminum Die Cast Plunger Tips | Mechanical Properties | Very High Strength | |
Corrosion Resistant Valves | Corrosion Resistance | Corrosion Resistance | |
Corrosion Resistant Valves | Corrosion Resistance | Corrosion Resistance to Most Chemical Environments | |
Corrosion Resistant Valves | Corrosion Resistance | Resists Stress Corrosion Cracking in Many Chemical Environments | |
Corrosion Resistant Valves | Corrosion Resistance | Resists Stress Corrosion Cracking in Marine Environments | |
Corrosion Resistant Valves | Friction & Wear Properties | Excellent Wear Resistance | |
Corrosion Resistant Valves | Mechanical Properties | Very High Strength | |
Glass Molds | Conductivity (Thermal) | Thermal Conductivity | |
Glass Molds | Corrosion Resistance | Corrosion Resistance | |
Glass Molds | Friction & Wear Properties | Wear Resistance | |
Glass Molds | Mechanical Properties | Very High Strength | |
Molds for Plastic Parts | Conductivity (Thermal) | Thermal Conductivity | |
Molds for Plastic Parts | Corrosion Resistance | Corrosion Resistance | |
Molds for Plastic Parts | Friction & Wear Properties | Wear Resistance | |
Molds for Plastic Parts | Mechanical Properties | Very High Strength | |
Permanent Molds for Brass and Aluminum Castings | Conductivity (Thermal) | Thermal Conductivity | |
Permanent Molds for Brass and Aluminum Castings | Corrosion Resistance | Corrosion Resistance | |
Permanent Molds for Brass and Aluminum Castings | Friction & Wear Properties | Wear Resistance | |
Permanent Molds for Brass and Aluminum Castings | Mechanical Properties | Very High Strength | |
Marine | Undersea Cable Housings | Conductivity (Electrical) | Electrical Conductivity |
Undersea Cable Housings | Corrosion Resistance | Corrosion Resistance | |
Undersea Cable Housings | Corrosion Resistance | Corrosion Resistance to Salt Water | |
Undersea Cable Housings | Mechanical Properties | Very High Strength |
Form | Specific Sub-Form | Application | System | Standard | Description |
---|---|---|---|---|---|
As Sand Cast | Castings | ASTM | B770 | COPPER-BERYLLIUM SAND CASTINGS | |
Ingot | ASTM | B30 | COPPER BASE ALLOYS IN INGOT FORM |
Corrosion Properties