C85300
Elements | |||||
---|---|---|---|---|---|
Cu(1) | Pb | Sn | Zn | P | |
(1) Cu + Sum of Named Elements 99.1% min. |
|||||
Min (%) | 68.0 | ||||
Max (%) | 72.0 | 0.50 | 0.50 | Rem | 0.50 |
Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.5% Ext (ksi) |
Elongation (%) |
Rockwell F scale |
---|---|---|---|---|---|---|
* Measured at room temperature, 68°F (20°C). | ||||||
As Sand Cast | As Sand Cast | M01 |
35 Typ |
11 Typ |
40 Typ |
54 Typ |
Melting Point - Liquidus°F | 1730 |
---|---|
Melting Point - Solidus°F | 1680 |
Densitylb/cu in. at 68°F | 0.308 |
Specific Gravity | 8.53 |
Electrical Conductivity% IACS at 68°F | 28 |
Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 70 |
Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 11.1 |
Specific Heat CapacityBtu/ lb /°F at 68°F | 0.09 |
Modulus of Elasticity in Tensionksi | 15000 |
Casting Attribute | Level |
---|---|
Casting Yield | Medium |
Drossing | High |
Effect of Section Size | Low |
Fluidity | Low |
Gassing | Low |
Patternmakers Shrinkage inches per inch | 3/16 |
Shrinkage in Solidification | High |
Technique | Suitability |
---|---|
Soldering | Excellent |
Brazing | Excellent |
Oxyacetylene Welding | Good |
Gas Shielded Arc Welding | Good |
Coated Metal Arc Welding | Not Recommended |
Machinability Rating | 30 |
Common Fabrication Processes
Treatment | Value* | Time** | ||
---|---|---|---|---|
* Temperature is measured in Fahrenheit. ** Time is measured in minutes. | ||||
Stress Relief | 500 | |||
Solution Treatment | 0 |
Typical Uses
Applicable Specifications
Corrosion Properties