C86200
| Elements | ||||||||
|---|---|---|---|---|---|---|---|---|
| Cu(1,2) | Pb | Sn | Zn | Fe | Ni(3) | Al | Mn | |
|
(1) Cu + Sum of Named Elements 99.0% min. (2) In determining Cu min., Cu may be calculated as Cu + Ni. (3) Ni value includes Co. |
||||||||
| Min (%) | 60.0 | 22.0 | 2.0 | 3.0 | 2.5 | |||
| Max (%) | 66.0 | 0.20 | 0.20 | 28.0 | 4.0 | 1.0 | 4.9 | 5.0 |
| Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.5% Ext (ksi) |
Elongation (%) |
Brinell Hardness, 3000 kg load | Izod (ft-lbs) |
Compressive Strength .001 in. set/in. (ksi) |
|---|---|---|---|---|---|---|---|---|
| * Measured at room temperature, 68°F (20°C). | ||||||||
| As Centrifugal Cast | As Centrifugal Cast | M02 |
90 Min for Standard |
|||||
| As Continuous Cast | As Continuous Cast | M07 |
90 Min for Standard |
45 Min for Standard |
18 Min for Standard |
|||
| As Sand Cast | As Sand Cast | M01 |
90 Min for Standard 95 Typ |
45 Min for Standard 48 Typ |
18 Min for Standard 20 Typ |
180 Typ |
12 Typ | 50 Typ |
| (1)Field Strength 16 kA/m | |
| Melting Point - Liquidus°F | 1725 |
|---|---|
| Melting Point - Solidus°F | 1650 |
| Densitylb/cu in. at 68°F | 0.288 |
| Specific Gravity | 7.97 |
| Electrical Conductivity% IACS at 68°F | 8 |
| Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 20.5 |
| Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 12 |
| Specific Heat CapacityBtu/ lb /°F at 68°F | 0.09 |
| Modulus of Elasticity in Tensionksi | 15000 |
| Magnetic Permeability | 1.24 (1) |
| Casting Attribute | Level |
|---|---|
| Casting Yield | Low |
| Drossing | High |
| Effect of Section Size | Low |
| Fluidity | Medium |
| Gassing | Low |
| Patternmakers Shrinkage inches per inch | 4/16 |
| Shrinkage in Solidification | High |
| Technique | Suitability |
|---|---|
| Soldering | Poor |
| Brazing | Poor |
| Oxyacetylene Welding | Good |
| Gas Shielded Arc Welding | Fair |
| Coated Metal Arc Welding | Good |
| Machinability Rating | 30 |
Common Fabrication Processes
No fabrication process properties for this alloy
| Treatment | Value* | Time** | ||
|---|---|---|---|---|
| * Temperature is measured in Fahrenheit. ** Time is measured in minutes. | ||||
| Stress Relief | 500 | |||
| Solution Treatment | 0 | |||
| Product Category | Product | Reason Category | Reason |
|---|---|---|---|
| Builders Hardware | Brackets | Corrosion Resistance | Corrosion Resistance |
| Brackets | Mechanical Properties | Moderate Strength | |
| Structural Parts | Corrosion Resistance | Corrosion Resistance | |
| Structural Parts | Mechanical Properties | Moderate Strength | |
| Fasteners | Screw Down Nuts | Corrosion Resistance | Corrosion Resistance |
| Screw Down Nuts | Friction & Wear Properties | Wear Resistance | |
| Screw Down Nuts | Mechanical Properties | Moderate Strength | |
| Industrial | Bushings | Corrosion Resistance | Corrosion Resistance |
| Bushings | Friction & Wear Properties | Wear Resistance | |
| Bushings | Mechanical Properties | Moderate Strength | |
| Cams | Corrosion Resistance | Corrosion Resistance | |
| Cams | Friction & Wear Properties | Wear Resistance | |
| Cams | Mechanical Properties | Moderate Strength | |
| Frames | Corrosion Resistance | Corrosion Resistance | |
| Frames | Friction & Wear Properties | Wear Resistance | |
| Frames | Mechanical Properties | Moderate Strength | |
| Gears | Corrosion Resistance | Corrosion Resistance | |
| Gears | Friction & Wear Properties | Wear Resistance | |
| Gears | Mechanical Properties | Moderate Strength | |
| High Strength Machine Parts | Conductivity (Thermal) | Thermal Conductivity | |
| High Strength Machine Parts | Corrosion Resistance | Corrosion Resistance | |
| High Strength Machine Parts | Corrosion Resistance | Corrosion Resistance to the Atmosphere | |
| High Strength Machine Parts | Friction & Wear Properties | Wear Resistance | |
| High Strength Machine Parts | Mechanical Properties | Moderate Strength | |
| Hooks | Corrosion Resistance | Corrosion Resistance | |
| Hooks | Mechanical Properties | Moderate Strength | |
| Marine Racing Propellers | Corrosion Resistance | Corrosion Resistance | |
| Marine Racing Propellers | Corrosion Resistance | Corrosion Resistance to Salt Water | |
| Marine Racing Propellers | Corrosion Resistance | Corrosion Resistance to the Atmosphere | |
| Marine Racing Propellers | Friction & Wear Properties | Wear Resistance | |
| Marine Racing Propellers | Mechanical Properties | Moderate Strength | |
| Pressing Dies for Wood Pulp | Corrosion Resistance | Corrosion Resistance | |
| Pressing Dies for Wood Pulp | Friction & Wear Properties | Wear Resistance | |
| Pressing Dies for Wood Pulp | Mechanical Properties | Moderate Strength | |
| Shafts | Corrosion Resistance | Corrosion Resistance | |
| Shafts | Friction & Wear Properties | Wear Resistance | |
| Shafts | Mechanical Properties | Moderate Strength | |
| Struts | Corrosion Resistance | Corrosion Resistance | |
| Struts | Corrosion Resistance | Corrosion Resistance to the Atmosphere | |
| Struts | Friction & Wear Properties | Wear Resistance | |
| Struts | Mechanical Properties | Moderate Strength | |
| Valve Stems | Corrosion Resistance | Corrosion Resistance | |
| Valve Stems | Friction & Wear Properties | Wear Resistance | |
| Valve Stems | Mechanical Properties | Moderate Strength | |
| Wear Rings for Pressing Dies for Wood Pulp Industry | Corrosion Resistance | Corrosion Resistance | |
| Wear Rings for Pressing Dies for Wood Pulp Industry | Friction & Wear Properties | Wear Resistance | |
| Wear Rings for Pressing Dies for Wood Pulp Industry | Mechanical Properties | Moderate Strength | |
| Worm Gears | Corrosion Resistance | Corrosion Resistance | |
| Worm Gears | Friction & Wear Properties | Wear Resistance | |
| Worm Gears | Mechanical Properties | Moderate Strength | |
| Marine | Boat Parts | Corrosion Resistance | Corrosion Resistance |
| Boat Parts | Corrosion Resistance | Corrosion Resistance to Salt Water | |
| Boat Parts | Corrosion Resistance | Corrosion Resistance to the Atmosphere | |
| Boat Parts | Friction & Wear Properties | Wear Resistance | |
| Boat Parts | Mechanical Properties | Moderate Strength | |
| Clamps | Corrosion Resistance | Corrosion Resistance | |
| Clamps | Corrosion Resistance | Corrosion Resistance to Salt Water | |
| Clamps | Mechanical Properties | Moderate Strength | |
| Marine Castings | Corrosion Resistance | Corrosion Resistance | |
| Marine Castings | Corrosion Resistance | Corrosion Resistance to Salt Water | |
| Marine Castings | Corrosion Resistance | Corrosion Resistance to the Atmosphere | |
| Marine Castings | Friction & Wear Properties | Wear Resistance | |
| Marine Castings | Mechanical Properties | Moderate Strength | |
| Rudders | Corrosion Resistance | Corrosion Resistance | |
| Rudders | Corrosion Resistance | Corrosion Resistance to Salt Water | |
| Rudders | Corrosion Resistance | Corrosion Resistance to the Atmosphere | |
| Rudders | Friction & Wear Properties | Wear Resistance | |
| Rudders | Mechanical Properties | Moderate Strength | |
| Ordnance | Gun Mounts | Appearance | Appearance |
| Gun Mounts | Corrosion Resistance | Corrosion Resistance | |
| Gun Mounts | Friction & Wear Properties | Wear Resistance | |
| Gun Mounts | Mechanical Properties | Moderate Strength |
| Form | Specific Sub-Form | Application | System | Standard | Description |
|---|---|---|---|---|---|
| As Centrifugal Cast | Castings | ASTM | B271/B271M | COPPER BASE ALLOY CENTRIFUGAL CASTINGS | |
| Castings | SAE | J462 | CAST COPPER ALLOYS | ||
| Castings | SAE | J461 | WROUGHT AND CAST COPPER ALLOYS | ||
| As Continuous Cast | Castings | SAE | J461 | WROUGHT AND CAST COPPER ALLOYS | |
| Castings | ASTM | B505/B505M | COPPER BASE ALLOY CONTINUOUS CASTINGS | ||
| Castings | SAE | J462 | CAST COPPER ALLOYS | ||
| As Sand Cast | Castings | ASTM | B584 | COPPER ALLOY SAND CASTINGS FOR GENERAL APPLICATIONS | |
| Castings | SAE | J461 | WROUGHT AND CAST COPPER ALLOYS | ||
| Castings | SAE | J462 | CAST COPPER ALLOYS | ||
| Castings | ASTM | B763/B763M | COPPER ALLOY SAND CASTINGS FOR VALVE APPLICATIONS | ||
| Ingot | ASTM | B30 | COPPER BASE ALLOYS IN INGOT FORM | ||
| FEDERAL | QQ-C-523 | COPPER ALLOY INGOTS: BRASS (YELLOW HIGH STRENGTH) MANGANESE AND MANGANESE-ALUMINUM BRONZE | |||
| Precision Cast | Castings | MILITARY | MIL-C-11866 | CASTINGS, PRECISION, NONFERROUS | |
| Valves |
Corrosion Properties
No Corrosion Properties Available.