Find suppliers for this alloy
C86300
Elements | ||||||||
---|---|---|---|---|---|---|---|---|
Cu(1,2) | Pb | Sn | Zn | Fe | Ni(3) | Al | Mn | |
(1) Cu + Sum of Named Elements 99.0% min. (2) In determining Cu min., Cu may be calculated as Cu + Ni. (3) Ni value includes Co. |
||||||||
Min (%) | 60.0 | 22.0 | 2.0 | 5.0 | 2.5 | |||
Max (%) | 66.0 | 0.20 | 0.20 | 28.0 | 4.0 | 1.0 | 7.5 | 5.0 |
Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.2% Offset (ksi) |
YS-0.5% Ext (ksi) |
Elongation (%) |
Brinell Hardness, 3000 kg load | Izod (ft-lbs) |
Charpy V-Notch Impact Strength (ft-lbs) |
Compressive Strength .001 in. set/in. (ksi) |
Compressive Strength .1 in. set/in. (ksi) |
Creep Strength (0.1% per 10,000 hours) (ksi) |
Fatigue Strength** (ksi) |
---|---|---|---|---|---|---|---|---|---|---|---|---|---|
* Measured at room temperature, 68°F (20°C). ** Fatigue Strength: 100 x 106 cycles, unless indicated as [N] x 106. | |||||||||||||
As Centrifugal Cast | As Centrifugal Cast | M02 |
110 Min for Standard |
83 Typ |
12 Min for Standard |
||||||||
As Continuous Cast | As Continuous Cast | M07 |
110 Min for Standard |
62 Min for Standard |
14 Min for Standard |
||||||||
As Sand Cast | As Sand Cast | M01 |
110 Min for Standard 119 Typ |
60 Min for Standard 62 Typ |
12 Min for Standard 18 Typ |
223 Min for Standard 225 Typ |
15 Typ | 12 Typ |
60 Typ | 97 Typ | 19 Typ | 25 Typ |
(1)Field Strength 16 kA/m | |
Melting Point - Liquidus°F | 1693 |
---|---|
Melting Point - Solidus°F | 1625 |
Densitylb/cu in. at 68°F | 0.283 |
Specific Gravity | 7.83 |
Electrical Conductivity% IACS at 68°F | 8 |
Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 20.5 |
Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 12 |
Specific Heat CapacityBtu/ lb /°F at 68°F | 0.09 |
Modulus of Elasticity in Tensionksi | 14200 |
Magnetic Permeability | 1.09 (1) |
Casting Attribute | Level |
---|---|
Casting Yield | Low |
Drossing | High |
Effect of Section Size | Low |
Fluidity | Medium |
Gassing | Low |
Patternmakers Shrinkage inches per inch | 4/16 |
Shrinkage in Solidification | High |
Technique | Suitability |
---|---|
Soldering | Poor |
Brazing | Poor |
Oxyacetylene Welding | Poor |
Gas Shielded Arc Welding | Poor |
Coated Metal Arc Welding | Good |
Machinability Rating | 8 |
Common Fabrication Processes
Treatment | Value* | Time** | ||
---|---|---|---|---|
* Temperature is measured in Fahrenheit. ** Time is measured in minutes. | ||||
Stress Relief | 500 | |||
Solution Treatment | 0 |
Product Category | Product | Reason Category | Reason |
---|---|---|---|
Builders Hardware | Brackets | Corrosion Resistance | Corrosion Resistance |
Brackets | Friction & Wear Properties | Wear Resistance | |
Brackets | Mechanical Properties | High Strength | |
Electrical | Electrical Components | Conductivity (Electrical) | Electrical Conductivity |
Electrical Components | Conductivity (Thermal) | Thermal Conductivity | |
Electrical Components | Corrosion Resistance | Corrosion Resistance | |
Electrical Components | Mechanical Properties | High Strength | |
Switches | Conductivity (Electrical) | Electrical Conductivity | |
Switches | Conductivity (Thermal) | Thermal Conductivity | |
Switches | Corrosion Resistance | Corrosion Resistance | |
Switches | Mechanical Properties | High Strength | |
Fasteners | Screw Down Nuts | Corrosion Resistance | Corrosion Resistance |
Screw Down Nuts | Corrosion Resistance | Corrosion Resistance | |
Screw Down Nuts | Mechanical Properties | High Strength | |
Screw Down Nuts | Mechanical Properties | High Strength | |
Industrial | Bridge Pins | Corrosion Resistance | Corrosion Resistance |
Bridge Pins | Friction & Wear Properties | Wear Resistance | |
Bridge Pins | Mechanical Properties | High Strength | |
Bushings | Corrosion Resistance | Corrosion Resistance | |
Bushings | Friction & Wear Properties | Wear Resistance | |
Bushings | Mechanical Properties | High Strength | |
Cams | Corrosion Resistance | Corrosion Resistance | |
Cams | Friction & Wear Properties | Wear Resistance | |
Cams | Mechanical Properties | High Strength | |
Forming Dies for Wood Pulp Industry | Corrosion Resistance | Corrosion Resistance | |
Forming Dies for Wood Pulp Industry | Friction & Wear Properties | Wear Resistance | |
Forming Dies for Wood Pulp Industry | Mechanical Properties | High Strength | |
Frames | Corrosion Resistance | Corrosion Resistance | |
Frames | Mechanical Properties | High Strength | |
Gears | Corrosion Resistance | Corrosion Resistance | |
Gears | Friction & Wear Properties | Wear Resistance | |
Gears | Mechanical Properties | High Strength | |
Gib | Corrosion Resistance | Corrosion Resistance | |
Gib | Friction & Wear Properties | Wear Resistance | |
Gib | Mechanical Properties | High Strength | |
High Strength Machine Parts | Conductivity (Thermal) | Thermal Conductivity | |
High Strength Machine Parts | Corrosion Resistance | Corrosion Resistance | |
High Strength Machine Parts | Friction & Wear Properties | Wear Resistance | |
High Strength Machine Parts | Mechanical Properties | High Strength | |
Hooks | Corrosion Resistance | Corrosion Resistance | |
Hooks | Mechanical Properties | High Strength | |
Hydraulic Cylinder Parts | Corrosion Resistance | Corrosion Resistance | |
Hydraulic Cylinder Parts | Friction & Wear Properties | Wear Resistance | |
Hydraulic Cylinder Parts | Mechanical Properties | High Strength | |
Large Valve Stems | Corrosion Resistance | Corrosion Resistance | |
Large Valve Stems | Friction & Wear Properties | Wear Resistance | |
Large Valve Stems | Mechanical Properties | High Strength | |
Propellers | Corrosion Resistance | Corrosion Resistance | |
Propellers | Friction & Wear Properties | Wear Resistance | |
Propellers | Mechanical Properties | High Strength | |
Slow Speed, Heavy Load Bearings | Corrosion Resistance | Corrosion Resistance | |
Slow Speed, Heavy Load Bearings | Friction & Wear Properties | Wear Resistance | |
Slow Speed, Heavy Load Bearings | Mechanical Properties | High Strength | |
Struts | Corrosion Resistance | Corrosion Resistance | |
Struts | Mechanical Properties | High Strength | |
Wear Rings for Forming Dies for Wood Pulp Industry | Corrosion Resistance | Corrosion Resistance | |
Wear Rings for Forming Dies for Wood Pulp Industry | Friction & Wear Properties | Wear Resistance | |
Wear Rings for Forming Dies for Wood Pulp Industry | Mechanical Properties | High Strength | |
Marine | Boat Parts | Corrosion Resistance | Corrosion Resistance |
Boat Parts | Corrosion Resistance | Corrosion Resistance to Salt Water | |
Boat Parts | Friction & Wear Properties | Wear Resistance | |
Boat Parts | Mechanical Properties | High Strength | |
Clamps | Corrosion Resistance | Corrosion Resistance | |
Clamps | Corrosion Resistance | Corrosion Resistance to Salt Water | |
Clamps | Friction & Wear Properties | Wear Resistance | |
Clamps | Mechanical Properties | High Strength | |
Covers for Marine Hardware | Appearance | Appearance | |
Covers for Marine Hardware | Corrosion Resistance | Corrosion Resistance | |
Covers for Marine Hardware | Corrosion Resistance | Corrosion Resistance to Salt Water | |
Covers for Marine Hardware | Friction & Wear Properties | Wear Resistance | |
Covers for Marine Hardware | Mechanical Properties | High Strength | |
Marine Hardware | Appearance | Appearance | |
Marine Hardware | Corrosion Resistance | Corrosion Resistance | |
Marine Hardware | Corrosion Resistance | Corrosion Resistance to Salt Water | |
Marine Hardware | Mechanical Properties | High Strength | |
Rudders | Corrosion Resistance | Corrosion Resistance | |
Rudders | Corrosion Resistance | Corrosion Resistance to Salt Water | |
Rudders | Friction & Wear Properties | Wear Resistance | |
Rudders | Mechanical Properties | High Strength |
Form | Specific Sub-Form | Application | System | Standard | Description |
---|---|---|---|---|---|
As Centrifugal Cast | Castings | SAE | J461 | WROUGHT AND CAST COPPER ALLOYS | |
Castings | SAE | J462 | CAST COPPER ALLOYS | ||
Castings | ASTM | B271/B271M | COPPER BASE ALLOY CENTRIFUGAL CASTINGS | ||
Castings | AMS | 4862 | MANGANESE BRONZE CASTINGS, SAND AND CENTRIFUGAL, HIGH STRENGTH, AS CAST | ||
As Continuous Cast | Castings | ASTM | B505/B505M | COPPER BASE ALLOY CONTINUOUS CASTINGS | |
As Sand Cast | Castings | ASTM | B584 | COPPER ALLOY SAND CASTINGS FOR GENERAL APPLICATIONS | |
Castings | ASTM | B763/B763M | COPPER ALLOY SAND CASTINGS FOR VALVE APPLICATIONS | ||
Castings | SAE | J462 | CAST COPPER ALLOYS | ||
Castings | SAE | J461 | WROUGHT AND CAST COPPER ALLOYS | ||
Castings | AMS | 4862 | MANGANESE BRONZE CASTINGS, SAND AND CENTRIFUGAL, HIGH STRENGTH, AS CAST | ||
Castings | ASTM | B22/B22M | BRONZE CASTINGS FOR BRIDGES AND TURNTABLES | ||
Ingot | FEDERAL | QQ-C-523 | COPPER ALLOY INGOTS: BRASS (YELLOW HIGH STRENGTH) MANGANESE AND MANGANESE-ALUMINUM BRONZE | ||
ASTM | B30 | COPPER BASE ALLOYS IN INGOT FORM | |||
Precision Cast | Castings | MILITARY | MIL-C-11866 | CASTINGS, PRECISION, NONFERROUS | |
Valves |
Corrosion Properties