C86500
Elements | ||||||||
---|---|---|---|---|---|---|---|---|
Cu(1,2) | Pb | Sn | Zn | Fe | Ni(3) | Al | Mn | |
(1) In determining Cu min., Cu may be calculated as Cu + Ni. (2) Cu + Sum of Named Elements 99.0% min. (3) Ni value includes Co. |
||||||||
Min (%) | 55.0 | 36.0 | 0.40 | 0.50 | 0.10 | |||
Max (%) | 60.0 | 0.40 | 1.0 | 42.0 | 2.0 | 1.0 | 1.5 | 1.5 |
Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.5% Ext (ksi) |
Elongation (%) |
Brinell Hardness, 500 kg load | Brinell Hardness, 3000 kg load | Izod (ft-lbs) |
Charpy V-Notch Impact Strength (ft-lbs) |
Compressive Strength .001 in. set/in. (ksi) |
Compressive Strength .1 in. set/in. (ksi) |
Creep Strength (0.1% per 10,000 hours) (ksi) |
Fatigue Strength** (ksi) |
---|---|---|---|---|---|---|---|---|---|---|---|---|---|
* Measured at room temperature, 68°F (20°C). ** Fatigue Strength: 100 x 106 cycles, unless indicated as [N] x 106. | |||||||||||||
As Centrifugal Cast | As Centrifugal Cast | M02 |
65 Min for Standard 65 Min for Standard |
25 Min for Standard |
20 Min for Standard 20 Min for Standard |
||||||||
As Continuous Cast | As Continuous Cast | M07 |
70 Min for Standard 70 Min for Standard |
25 Min for Standard |
25 Min for Standard 25 Min for Standard |
||||||||
As Sand Cast | As Sand Cast | M01 |
65 Min for Standard 71 Typ |
25 Min for Standard 29 Typ |
20 Min for Standard 30 Typ |
100 Typ |
130 Typ |
32 Typ | 32 Typ |
24 Typ | 79 Typ | 28 Typ | 20 Typ |
(1)Field Strength 16kA/m | |
Melting Point - Liquidus°F | 1616 |
---|---|
Melting Point - Solidus°F | 1583 |
Densitylb/cu in. at 68°F | 0.301 |
Specific Gravity | 8.33 |
Electrical Conductivity% IACS at 68°F | 22 |
Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 49.6 |
Coefficient of Thermal Expansion 68-21210 to -6 power per °F (68 – 212°F) | 11.3 |
Specific Heat CapacityBtu/ lb /°F at 68°F | 0.09 |
Modulus of Elasticity in Tensionksi | 15000 |
Magnetic Permeability | 1.09 (1) |
Casting Attribute | Level |
---|---|
Casting Yield | Low |
Drossing | High |
Effect of Section Size | Low |
Fluidity | Medium |
Gassing | Low |
Patternmakers Shrinkage inches per inch | 4/16 |
Shrinkage in Solidification | High |
Technique | Suitability |
---|---|
Soldering | Fair |
Brazing | Fair |
Oxyacetylene Welding | Poor |
Gas Shielded Arc Welding | Poor |
Coated Metal Arc Welding | Poor |
Machinability Rating | 26 |
Common Fabrication Processes
Treatment | Value* | Time** | ||
---|---|---|---|---|
* Temperature is measured in Fahrenheit. ** Time is measured in minutes. | ||||
Stress Relief | 500 | |||
Solution Treatment | 0 |
Product Category | Product | Reason Category | Reason |
---|---|---|---|
Automotive | Weld Guns | Conductivity (Thermal) | Thermal Conductivity |
Weld Guns | Corrosion Resistance | Corrosion Resistance | |
Weld Guns | Mechanical Properties | High Strength | |
Builders Hardware | Brackets | Corrosion Resistance | Corrosion Resistance |
Brackets | Mechanical Properties | High Strength | |
Brackets | Mechanical Properties | Toughness | |
Electrical | Electrical Hardware | Conductivity (Electrical) | Electrical Conductivity |
Electrical Hardware | Conductivity (Thermal) | Thermal Conductivity | |
Electrical Hardware | Corrosion Resistance | Corrosion Resistance | |
Electrical Hardware | Mechanical Properties | High Strength | |
Industrial | Compressors | Corrosion Resistance | Corrosion Resistance |
Compressors | Mechanical Properties | High Strength | |
Compressors | Mechanical Properties | Toughness | |
Forming Dies for Wood Pulp Industry | Corrosion Resistance | Corrosion Resistance | |
Forming Dies for Wood Pulp Industry | Friction & Wear Properties | Wear Resistance | |
Forming Dies for Wood Pulp Industry | Mechanical Properties | High Strength | |
Forming Dies for Wood Pulp Industry | Mechanical Properties | Toughness | |
Frames | Machining Characteristics | Excellent Machinability (Free Machining) | |
Frames | Mechanical Properties | High Strength | |
Gears | Corrosion Resistance | Corrosion Resistance | |
Gears | Corrosion Resistance | Corrosion Resistance to Fresh Water | |
Gears | Corrosion Resistance | Corrosion Resistance to Salt Water | |
Gears | Mechanical Properties | High Strength | |
Gears | Mechanical Properties | Toughness | |
Hooks | Corrosion Resistance | Corrosion Resistance | |
Hooks | Mechanical Properties | High Strength | |
Hooks | Mechanical Properties | Toughness | |
Lever Arms | Corrosion Resistance | Corrosion Resistance | |
Lever Arms | Mechanical Properties | High Strength | |
Lever Arms | Mechanical Properties | Toughness | |
Machinery | Conductivity (Thermal) | Thermal Conductivity | |
Machinery | Corrosion Resistance | Corrosion Resistance | |
Machinery | Mechanical Properties | High Strength | |
Machinery | Mechanical Properties | Toughness | |
Machinery Parts (Substituted for Steel and Malleable Iron) | Corrosion Resistance | Corrosion Resistance | |
Machinery Parts (Substituted for Steel and Malleable Iron) | Mechanical Properties | High Strength | |
Machinery Parts (Substituted for Steel and Malleable Iron) | Mechanical Properties | Toughness | |
Machinery Parts requiring High Strength | Conductivity (Thermal) | Thermal Conductivity | |
Machinery Parts requiring High Strength | Corrosion Resistance | Corrosion Resistance | |
Machinery Parts requiring High Strength | Mechanical Properties | High Strength | |
Machinery Parts requiring High Strength | Mechanical Properties | Toughness | |
Pressing Dies for Wood Pulp | Corrosion Resistance | Corrosion Resistance | |
Pressing Dies for Wood Pulp | Friction & Wear Properties | Wear Resistance | |
Pressing Dies for Wood Pulp | Mechanical Properties | High Strength | |
Pressing Dies for Wood Pulp | Mechanical Properties | Toughness | |
Struts | Corrosion Resistance | Corrosion Resistance | |
Struts | Mechanical Properties | High Strength | |
Struts | Mechanical Properties | Toughness | |
Wear Rings for Pressing Dies for Wood Pulp Industry | Corrosion Resistance | Corrosion Resistance | |
Wear Rings for Pressing Dies for Wood Pulp Industry | Friction & Wear Properties | Wear Resistance | |
Wear Rings for Pressing Dies for Wood Pulp Industry | Mechanical Properties | High Strength | |
Wear Rings for Pressing Dies for Wood Pulp Industry | Mechanical Properties | Toughness | |
Marine | Boat Parts | Corrosion Resistance | Corrosion Resistance |
Boat Parts | Corrosion Resistance | Corrosion Resistance to Salt Water | |
Boat Parts | Mechanical Properties | High Strength | |
Clamps | Corrosion Resistance | Corrosion Resistance | |
Clamps | Corrosion Resistance | Corrosion Resistance to Salt Water | |
Clamps | Mechanical Properties | High Strength | |
Clamps | Mechanical Properties | Toughness | |
Covers for Marine Hardware | Appearance | Appearance | |
Covers for Marine Hardware | Corrosion Resistance | Corrosion Resistance | |
Covers for Marine Hardware | Corrosion Resistance | Corrosion Resistance to Salt Water | |
Covers for Marine Hardware | Mechanical Properties | High Strength | |
Propellers for salt and fresh water | Corrosion Resistance | Corrosion Resistance | |
Propellers for salt and fresh water | Corrosion Resistance | Corrosion Resistance to Saline Solutions | |
Propellers for salt and fresh water | Corrosion Resistance | Corrosion Resistance to Salt Water | |
Propellers for salt and fresh water | Mechanical Properties | Ductility | |
Propellers for salt and fresh water | Mechanical Properties | High Strength | |
Rudders | Corrosion Resistance | Corrosion Resistance | |
Rudders | Corrosion Resistance | Corrosion Resistance to Salt Water | |
Rudders | Friction & Wear Properties | Wear Resistance | |
Rudders | Mechanical Properties | High Strength |
Form | Specific Sub-Form | Application | System | Standard | Description |
---|---|---|---|---|---|
As Centrifugal Cast | Castings | ASTM | B271/B271M | COPPER BASE ALLOY CENTRIFUGAL CASTINGS | |
Castings | AMS | 4860 | MANGANESE BRONZE CASTINGS, SAND AND CENTRIFUGAL, AS CAST | ||
Castings | SAE | J462 | CAST COPPER ALLOYS | ||
Castings | SAE | J461 | WROUGHT AND CAST COPPER ALLOYS | ||
As Continuous Cast | Castings | ASTM | B505/B505M | COPPER BASE ALLOY CONTINUOUS CASTINGS | |
As Die Cast | Castings | ASTM | B176 | BRASS DIE CASTINGS | |
As Sand Cast | Castings | AMS | 4860 | MANGANESE BRONZE CASTINGS, SAND AND CENTRIFUGAL, AS CAST | |
Castings | SAE | J462 | CAST COPPER ALLOYS | ||
Castings | ASTM | B584 | COPPER ALLOY SAND CASTINGS FOR GENERAL APPLICATIONS | ||
Castings | SAE | J461 | WROUGHT AND CAST COPPER ALLOYS | ||
Castings | ASTM | B763/B763M | COPPER ALLOY SAND CASTINGS FOR VALVE APPLICATIONS | ||
Ingot | ASTM | B30 | COPPER BASE ALLOYS IN INGOT FORM | ||
FEDERAL | QQ-C-523 | COPPER ALLOY INGOTS: BRASS (YELLOW HIGH STRENGTH) MANGANESE AND MANGANESE-ALUMINUM BRONZE | |||
Valves |
Corrosion Properties