Find suppliers for this alloyC86500
Chemical Composition
Element
Cu(1,2)PbSnZnFeNi(3)AlMn
(1) In determining Cu min., Cu may be calculated as Cu + Ni. (2) Cu + Sum of Named Elements 99.0% min. (3) Ni value includes Co.
Min (%)55.036.00.400.500.10
Max (%)60.00.401.042.02.01.01.51.5
Mechanical Properties*
Form
Temper
Temper Code
Tensile Strength
(ksi)
YS-0.5% Ext
(ksi)
Elongation
(%)
Brinell Hardness, 500 kg load
Brinell Hardness, 3000 kg load
Izod
(ft-lbs)
Charpy V-Notch Impact Strength
(ft-lbs)
Compressive Strength .001 in. set/in.
(ksi)
Compressive Strength .1 in. set/in.
(ksi)
Creep Strength (0.1% per 10,000 hours)
(ksi)
Fatigue Strength**
(ksi)
As Centrifugal CastAs Centrifugal CastM0265   Min for Standard
65   Min for Standard
25   Min for Standard
25   Min for Standard
20   Min for Standard
20   Min for Standard
As Continuous CastAs Continuous CastM0770   Min for Standard
70   Min for Standard
25   Min for Standard
25   Min for Standard
25   Min for Standard
25   Min for Standard
As Sand CastAs Sand CastM0165   Min for Standard
71   Typ
25   Min for Standard
29   Typ
20   Min for Standard
30   Typ
100   Typ
130   Typ
32   Typ
32   Typ
24   Typ
79   Typ
28   Typ
1.7   Typ
6.2   Typ
20   Typ
* Measured at room temperature, 68°F (20°C). ** Fatigue Strength: 100 x 106 cycles, unless indicated as [N] x 106.
Physical Properties
(1) Field Strength 16kA/m
Melting Point - Liquidus°F1616
Melting Point - Solidus°F1583
Densitylb/cu in. at 68°F0.301
Specific Gravity8.33
Electrical Conductivity% IACS at 68°F22
Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F49.6
Coefficient of Thermal Expansion 68-21210⁻⁶ per °F (68 – 212°F)11.3
Specific Heat CapacityBtu/ lb /°F at 68°F0.09
Modulus of Elasticity in Tensionksi15000
Magnetic Permeability1.09(1)
Casting Characteristics
Casting Attribute Level
Casting YieldLow
DrossingHigh
Effect of Section SizeLow
FluidityMedium
GassingLow
Patternmakers Shrinkageinches per inch4/16
Shrinkage in SolidificationHigh
Fabrication Properties
Technique Suitability
SolderingFair
BrazingFair
Oxyacetylene WeldingPoor
Gas Shielded Arc WeldingPoor
Coated Metal Arc WeldingPoor
Machinability Rating26
Common Fabrication Processes
  • Casting
    
Thermal Properties
Treatment Value* Time**
* Temperature is measured in Fahrenheit. ** Time is measured in minutes.
Stress Relief500
Solution Treatment0
Typical uses
Product Category Product Reason Category Reason
AutomotiveWeld GunsConductivity (Thermal)Thermal Conductivity
Weld GunsCorrosion ResistanceCorrosion Resistance
Weld GunsMechanical PropertiesHigh Strength
Builders HardwareBracketsCorrosion ResistanceCorrosion Resistance
BracketsMechanical PropertiesHigh Strength
BracketsMechanical PropertiesToughness
ElectricalElectrical HardwareConductivity (Electrical)Electrical Conductivity
Electrical HardwareConductivity (Thermal)Thermal Conductivity
Electrical HardwareCorrosion ResistanceCorrosion Resistance
Electrical HardwareMechanical PropertiesHigh Strength
IndustrialCompressorsCorrosion ResistanceCorrosion Resistance
CompressorsMechanical PropertiesHigh Strength
CompressorsMechanical PropertiesToughness
Forming Dies for Wood Pulp IndustryCorrosion ResistanceCorrosion Resistance
Forming Dies for Wood Pulp IndustryFriction & Wear PropertiesWear Resistance
Forming Dies for Wood Pulp IndustryMechanical PropertiesHigh Strength
Forming Dies for Wood Pulp IndustryMechanical PropertiesToughness
FramesMachining CharacteristicsExcellent Machinability (Free Machining)
FramesMechanical PropertiesHigh Strength
GearsCorrosion ResistanceCorrosion Resistance
GearsCorrosion ResistanceCorrosion Resistance to Fresh Water
GearsCorrosion ResistanceCorrosion Resistance to Salt Water
GearsMechanical PropertiesHigh Strength
GearsMechanical PropertiesToughness
HooksCorrosion ResistanceCorrosion Resistance
HooksMechanical PropertiesHigh Strength
HooksMechanical PropertiesToughness
Lever ArmsCorrosion ResistanceCorrosion Resistance
Lever ArmsMechanical PropertiesHigh Strength
Lever ArmsMechanical PropertiesToughness
MachineryConductivity (Thermal)Thermal Conductivity
MachineryCorrosion ResistanceCorrosion Resistance
MachineryMechanical PropertiesHigh Strength
MachineryMechanical PropertiesToughness
Machinery Parts (Substituted for Steel and Malleable Iron)Corrosion ResistanceCorrosion Resistance
Machinery Parts (Substituted for Steel and Malleable Iron)Mechanical PropertiesHigh Strength
Machinery Parts (Substituted for Steel and Malleable Iron)Mechanical PropertiesToughness
Machinery Parts requiring High StrengthConductivity (Thermal)Thermal Conductivity
Machinery Parts requiring High StrengthCorrosion ResistanceCorrosion Resistance
Machinery Parts requiring High StrengthMechanical PropertiesHigh Strength
Machinery Parts requiring High StrengthMechanical PropertiesToughness
Pressing Dies for Wood PulpCorrosion ResistanceCorrosion Resistance
Pressing Dies for Wood PulpFriction & Wear PropertiesWear Resistance
Pressing Dies for Wood PulpMechanical PropertiesHigh Strength
Pressing Dies for Wood PulpMechanical PropertiesToughness
StrutsCorrosion ResistanceCorrosion Resistance
StrutsMechanical PropertiesHigh Strength
StrutsMechanical PropertiesToughness
Wear Rings for Pressing Dies for Wood Pulp IndustryCorrosion ResistanceCorrosion Resistance
Wear Rings for Pressing Dies for Wood Pulp IndustryFriction & Wear PropertiesWear Resistance
Wear Rings for Pressing Dies for Wood Pulp IndustryMechanical PropertiesHigh Strength
Wear Rings for Pressing Dies for Wood Pulp IndustryMechanical PropertiesToughness
MarineBoat PartsCorrosion ResistanceCorrosion Resistance
Boat PartsCorrosion ResistanceCorrosion Resistance to Salt Water
Boat PartsMechanical PropertiesHigh Strength
ClampsCorrosion ResistanceCorrosion Resistance
ClampsCorrosion ResistanceCorrosion Resistance to Salt Water
ClampsMechanical PropertiesHigh Strength
ClampsMechanical PropertiesToughness
Covers for Marine HardwareAppearanceAppearance
Covers for Marine HardwareCorrosion ResistanceCorrosion Resistance
Covers for Marine HardwareCorrosion ResistanceCorrosion Resistance to Salt Water
Covers for Marine HardwareMechanical PropertiesHigh Strength
Propellers for salt and fresh waterCorrosion ResistanceCorrosion Resistance
Propellers for salt and fresh waterCorrosion ResistanceCorrosion Resistance to Saline Solutions
Propellers for salt and fresh waterCorrosion ResistanceCorrosion Resistance to Salt Water
Propellers for salt and fresh waterMechanical PropertiesDuctility
Propellers for salt and fresh waterMechanical PropertiesHigh Strength
RuddersCorrosion ResistanceCorrosion Resistance
RuddersCorrosion ResistanceCorrosion Resistance to Salt Water
RuddersFriction & Wear PropertiesWear Resistance
RuddersMechanical PropertiesHigh Strength
Applicable Specifications
Form Sub-Form System Standard Description
As Centrifugal CastCastingsAMS4860MANGANESE BRONZE CASTINGS, SAND AND CENTRIFUGAL, AS CAST
CastingsASTMB271/B271MCOPPER BASE ALLOY CENTRIFUGAL CASTINGS
CastingsSAEJ461WROUGHT AND CAST COPPER ALLOYS
CastingsSAEJ462CAST COPPER ALLOYS
As Continuous CastCastingsASTMB505/B505MCOPPER BASE ALLOY CONTINUOUS CASTINGS
As Die CastCastingsASTMB176BRASS DIE CASTINGS
As Sand CastCastingsAMS4860MANGANESE BRONZE CASTINGS, SAND AND CENTRIFUGAL, AS CAST
CastingsASTMB584COPPER ALLOY SAND CASTINGS FOR GENERAL APPLICATIONS
CastingsASTMB763/B763MCOPPER ALLOY SAND CASTINGS FOR VALVE APPLICATIONS
CastingsSAEJ461WROUGHT AND CAST COPPER ALLOYS
CastingsSAEJ462CAST COPPER ALLOYS
Ingot
ASTMB30COPPER BASE ALLOYS IN INGOT FORM
FEDERALQQ-C-523COPPER ALLOY INGOTS: BRASS (YELLOW HIGH STRENGTH) MANGANESE AND MANGANESE-ALUMINUM BRONZE
Valves
Corrosion Properties

No information available.