Find suppliers for this alloyC87200
Chemical Composition
Element
CuPbSnZnFePAlMnSi
Min (%)89.01.0
Max (%)0.501.05.02.50.501.51.55.0
Mechanical Properties*
Form
Temper
Temper Code
Tensile Strength
(ksi)
YS-0.5% Ext
(ksi)
Elongation
(%)
Brinell Hardness, 500 kg load
Shear Strength
(ksi)
Izod
(ft-lbs)
Compressive Strength .001 in. set/in.
(ksi)
Compressive Strength .01 in. set/in.
(ksi)
As Centrifugal CastAs Centrifugal CastM0245   Min for Standard
18   Min for Standard
20   Min for Standard
As Sand CastAs Sand CastM0145   Min for Standard
55   Typ
18   Min for Standard
25   Typ
20   Min for Standard
30   Typ
85   Typ
28   Typ
33   Typ
18   Typ
60   Typ
* Measured at room temperature, 68°F (20°C).
Physical Properties
Melting Point - Liquidus°F1780
Melting Point - Solidus°F1580
Densitylb/cu in. at 68°F0.302
Specific Gravity8.4
Electrical Conductivity% IACS at 68°F6
Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F16.4
Specific Heat CapacityBtu/ lb /°F at 68°F0.09
Modulus of Elasticity in Tensionksi15000
Casting Characteristics
Casting Attribute Level
Casting YieldMedium
DrossingLow
Effect of Section SizeMedium
FluidityHigh
GassingHigh
Patternmakers Shrinkageinches per inch4/16
Shrinkage in SolidificationMedium
Fabrication Properties
Technique Suitability
SolderingNot Recommended
BrazingFair
Oxyacetylene WeldingGood
Gas Shielded Arc WeldingFair
Coated Metal Arc WeldingFair
Machinability Rating40
Fabrication Process Properties

No fabrication process properties for this alloy

    
Thermal Properties
Treatment Value* Time**
* Temperature is measured in Fahrenheit. ** Time is measured in minutes.
Stress Relief500
Solution Treatment0
Typical uses
Product Category Product Reason Category Reason
Builders HardwareWindow HardwareAppearanceAppearance
Window HardwareCorrosion ResistanceCorrosion Resistance
Window HardwareMechanical PropertiesModerate Strength
Applicable Specifications

No applicable specifications for this alloy

Corrosion Properties

No information available.