C87610
| Elements | ||||||
|---|---|---|---|---|---|---|
| Cu(1) | Pb | Zn | Fe | Mn | Si | |
|
(1) Cu + Sum of Named Elements 99.5% min. |
||||||
| Min (%) | 90.0 | 3.0 | 3.0 | |||
| Max (%) | 0.09 | 5.0 | 0.20 | 0.25 | 5.0 | |
| Form | Temper | Temper Code | Tensile Strength (ksi) |
Elongation (%) |
Rockwell B scale | Brinell Hardness, 500 kg load | Brinell Hardness, 3000 kg load | Shear Strength (ksi) |
Izod (ft-lbs) |
Compressive Strength .001 in. set/in. (ksi) |
Compressive Strength .01 in. set/in. (ksi) |
|---|---|---|---|---|---|---|---|---|---|---|---|
| * Measured at room temperature, 68°F (20°C). | |||||||||||
| As Centrifugal Cast | As Centrifugal Cast | M02 |
45 Min for Standard |
20 Min for Standard |
|||||||
| As Sand Cast | As Sand Cast | M01 |
45 Min for Standard 58 Typ |
20 Min for Standard 35 Typ |
76 Typ |
96 Typ |
135 Typ |
28 Typ |
33 Typ | 19 Typ | 60 Typ |
| Melting Point - Liquidus°F | 1780 |
|---|---|
| Melting Point - Solidus°F | 1510 |
| Densitylb/cu in. at 68°F | 0.302 |
| Specific Gravity | 8.36 |
| Electrical Conductivity% IACS at 68°F | 6.1 |
| Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 16.4 |
| Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 11 |
| Modulus of Elasticity in Tensionksi | 16000 |
Casting Characteristics
No casting characteristics for this alloy
| Technique | Suitability |
|---|---|
| Soldering | Excellent |
| Brazing | Excellent |
| Oxyacetylene Welding | Fair |
| Gas Shielded Arc Welding | Excellent |
| Coated Metal Arc Welding | Good |
| Spot Weld | Good |
| Seam Weld | Good |
| Butt Weld | Good |
| Machinability Rating | 40 |
Common Fabrication Processes
No fabrication process properties for this alloy
Thermal Properties
No thermal properties for this alloy
| Product Category | Product | Reason Category | Reason |
|---|---|---|---|
| Architecture | Statuary | Appearance | Appearance |
| Statuary | Casting Characteristics | Castability | |
| Statuary | Corrosion Resistance | Corrosion Resistance | |
| Statuary | Mechanical Properties | High Strength | |
| Consumer | Decorative Pieces | Appearance | Appearance |
| Decorative Pieces | Casting Characteristics | Castability | |
| Decorative Pieces | Corrosion Resistance | Corrosion Resistance | |
| Decorative Pieces | Mechanical Properties | High Strength | |
| Industrial | Pump Components | Corrosion Resistance | Corrosion Resistance |
| Pump Components | Corrosion Resistance | Corrosion Resistance to Salt Water | |
| Pump Components | Mechanical Properties | Ductility | |
| Pump Components | Mechanical Properties | High Strength | |
| Valve Stems | Corrosion Resistance | Corrosion Resistance | |
| Valve Stems | Mechanical Properties | Ductility | |
| Valve Stems | Mechanical Properties | High Strength |
| Form | Specific Sub-Form | Application | System | Standard | Description |
|---|---|---|---|---|---|
| As Sand Cast | Castings | ASTM | B584 | COPPER ALLOY SAND CASTINGS FOR GENERAL APPLICATIONS | |
| ASTM | B763/B763M | COPPER ALLOY SAND CASTINGS FOR VALVE APPLICATIONS | |||
| Ingot | |||||
| ASTM | B30 | COPPER BASE ALLOYS IN INGOT FORM |
Corrosion Properties
No Corrosion Properties Available.