C89325
| Elements | ||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Cu(1,2) | Pb | Sn | Zn | Fe | P | Ni(3) | Al | Bi | S | Sb | Si | |
|
(1) Cu + Sum of Named Elements 99.0% min. (2) 0.01 - 2.0% as any single or combination of Ce La or other rare earth(x) elements as agreed upon. (x)ASM International definition: one of the group of chemically similar metals with atomic numbers 57 through 71 commonly refered to as lanthanides (3) Ni value includes Co. |
||||||||||||
| Min (%) | 84.0 | 9.0 | 2.7 | |||||||||
| Max (%) | 88.0 | 0.10 | 11.0 | 1.0 | 0.15 | 0.10 | 1.0 | 0.005 | 3.7 | 0.08 | 0.50 | 0.005 |
| Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.5% Ext (ksi) |
Elongation (%) |
Brinell Hardness, 500 kg load | Izod (ft-lbs) |
|---|---|---|---|---|---|---|---|
| * Measured at room temperature, 68°F (20°C). | |||||||
| As Sand Cast | As Sand Cast | M01 |
35 Typ |
18 Typ |
20 Typ |
73 Typ |
6 Typ |
| Melting Point - Liquidus°F | 1805 |
|---|---|
| Melting Point - Solidus°F | 1432 |
| Densitylb/cu in. at 68°F | 0.323 |
| Specific Gravity | 8.94 |
| Electrical Conductivity% IACS at 68°F | 10.8 |
| Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 29 |
| Coefficient of Thermal Expansion 68-39210 to -6 power per °F (68 – 392°F) | 10.3 |
| Specific Heat CapacityBtu/ lb /°F at 68°F | 0.089 |
| Modulus of Elasticity in Tensionksi | 16400 |
| Casting Attribute | Level |
|---|---|
| Casting Yield | High |
| Drossing | Low |
| Effect of Section Size | Low |
| Fluidity | Medium |
| Gassing | Medium |
| Patternmakers Shrinkage inches per inch | 3/32 |
| Shrinkage in Solidification | Low |
| Technique | Suitability |
|---|---|
| Soldering | Good |
| Brazing | Good |
| Oxyacetylene Welding | Not Recommended |
| Gas Shielded Arc Welding | Not Recommended |
| Coated Metal Arc Welding | Not Recommended |
| Machinability Rating | 80 |
Common Fabrication Processes
No fabrication process properties for this alloy
Thermal Properties
No thermal properties for this alloy
| Product Category | Product | Reason Category | Reason |
|---|---|---|---|
| Industrial | Bushings | Corrosion Resistance | Corrosion Resistance |
| Bushings | Friction & Wear Properties | Wear Resistance | |
| Bushings | Lead Free | Lead-Free Alternative to Leaded Alloy C93700 | |
| Bushings | Mechanical Properties | Moderate Strength | |
| High Speed, High Pressure Bearings | Corrosion Resistance | Corrosion Resistance | |
| High Speed, High Pressure Bearings | Friction & Wear Properties | Wear Resistance | |
| High Speed, High Pressure Bearings | Lead Free | Lead-Free Alternative to Leaded Alloy C93700 | |
| High Speed, High Pressure Bearings | Mechanical Properties | Moderate Strength |
Applicable Specifications
No applicable specifications for this alloy
Corrosion Properties
No Corrosion Properties Available.