Find suppliers for this alloy
C89510
Elements | |||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Cu(1) | Pb | Sn | Zn | Fe | P | Ni(2) | Al | Bi(3) | S | Sb | Si | Se(4) | |
(1) Cu + Sum of Named Elements 99.5% min. (2) Ni value includes Co. (3) Experience favors Bi:Se >= 2:1 (4) Experience favors Bi:Se >= 2:1 |
|||||||||||||
Min (%) | 86.0 | 4.0 | 4.0 | 0.50 | 0.35 | ||||||||
Max (%) | 88.0 | 0.09 | 6.0 | 6.0 | 0.20 | 0.05 | 1.0 | 0.005 | 1.5 | 0.08 | 0.25 | 0.005 | 0.75 |
Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.5% Ext (ksi) |
Elongation (%) |
Brinell Hardness, 500 kg load |
---|---|---|---|---|---|---|
* Measured at room temperature, 68°F (20°C). | ||||||
As Sand Cast | As Sand Cast | M01 |
30 Typ |
20 Typ |
12 Typ |
37 Typ |
Melting Point - Liquidus°F | 1871 |
---|---|
Melting Point - Solidus°F | 1500 |
Densitylb/cu in. at 68°F | 0.313 |
Specific Gravity | 8.66 |
Casting Attribute | Level |
---|---|
Casting Yield | High |
Drossing | Low |
Effect of Section Size | Low |
Fluidity | Medium |
Gassing | Medium |
Shrinkage in Solidification | Medium |
Technique | Suitability |
---|---|
Soldering | Excellent |
Brazing | Good |
Oxyacetylene Welding | Not Recommended |
Gas Shielded Arc Welding | Not Recommended |
Coated Metal Arc Welding | Not Recommended |
Machinability Rating | 75 |
Common Fabrication Processes
Thermal Properties
Product Category | Product | Reason Category | Reason |
---|---|---|---|
Plumbing | Plumbing Castings | Corrosion Resistance | Corrosion Resistance |
Plumbing Castings | Lead Free | Lead Free | |
Plumbing Castings | Machining Properties | Machinability, Good | |
Plumbing Castings | Mechanical Properties | Moderate Strength |
Form | Specific Sub-Form | Application | System | Standard | Description |
---|---|---|---|---|---|
As Sand Cast | ASTM | B584 | COPPER ALLOY SAND CASTINGS FOR GENERAL APPLICATIONS | ||
Ingot | ASTM | B30 | COPPER BASE ALLOYS IN INGOT FORM |
Corrosion Properties