C89580
Elements | ||||||||
---|---|---|---|---|---|---|---|---|
Cu(1) | Pb | Sn | Zn | Fe | Ni(2) | Al | Bi | |
(1) Cu + Sum of Named Elements 99.5% min. (2) Ni value includes Co. |
||||||||
Min (%) | 57.0 | .10 | .10 | |||||
Max (%) | 64.0 | .09 | .50 | Rem | .10 | .30 | 1.2 | 1.0 |
Form | Temper | Temper Code | Tensile Strength (ksi) |
Elongation (%) |
Brinell Hardness, 3000 kg load |
---|---|---|---|---|---|
* Measured at room temperature, 68°F (20°C). | |||||
As Permanent Mold Cast | As Permanent Mold Cast | M05 |
50.8 Min 54.4 Typ 58.0 Max |
10 Min 25 Max |
60 Min 100 Max |
As Sand Cast | As Sand Cast | M01 |
50.8 Min 54.4 Typ 58.0 Max |
10 Min 25 Max |
60 Min 100 Max |
Melting Point - Solidus°F | 1621 |
---|---|
Densitylb/cu in. at 68°F | 0.298 |
Specific Gravity | 8.24 |
Electrical Conductivity% IACS at 68°F | 21 |
Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 58.7 |
Coefficient of Thermal Expansion 68-21210 to -6 power per °F (68 – 212°F) | 11.41 |
Coefficient of Thermal Expansion 68-39210 to -6 power per °F (68 – 392°F) | 11.76 |
Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 11.73 |
Specific Heat CapacityBtu/ lb /°F at 68°F | 0.093 |
Modulus of Elasticity in Tensionksi | 12910 |
Modulus of Rigidityksi | 4640 |
Poisson's Ratio | 0.39 |
Casting Characteristics
Technique | Suitability |
---|---|
Soldering | Fair |
Brazing | Poor |
Oxyacetylene Welding | Poor |
Gas Shielded Arc Welding | Fair |
Coated Metal Arc Welding | Fair |
Spot Weld | Fair |
Seam Weld | Poor |
Butt Weld | Fair |
Capacity for Being Cold Worked | Poor |
Capacity for Being Hot Formed | Excellent |
Common Fabrication Processes
Thermal Properties
Typical Uses
Applicable Specifications
Corrosion Properties