C89710
| Elements | ||||||||||
|---|---|---|---|---|---|---|---|---|---|---|
| Cu(1) | Pb | Sn | Zn | P | Al | B | Bi | Mn | Sb | |
|
(1) Cu + Sum of Named Elements 99.8% min. |
||||||||||
| Min (%) | 61.5 | 0.50 | 0.15 | 0.15 | 0.002 | 0.15 | 0.20 | 0.25 | ||
| Max (%) | 62.5 | 0.10 | 0.6 | Rem | 0.20 | 0.25 | 0.005 | 0.30 | 0.40 | 0.35 |
| Form | Temper | Temper Code | YS-0.2% Offset (ksi) |
Elongation (%) |
Brinell Hardness, 3000 kg load | Shear Strength (ksi) |
Compressive Yield Strength (ksi) |
Ultimate Tensile Strength in Shear (ksi) |
|---|---|---|---|---|---|---|---|---|
| * Measured at room temperature, 68°F (20°C). | ||||||||
| As Permanent Mold Cast | As Permanent Mold Cast | M05 | 22.5 Typ |
39 Typ |
73 Typ |
35.8 Typ |
374.5 Typ | 52.6 Typ |
| Melting Point - Liquidus°F | 1697 |
|---|---|
| Melting Point - Solidus°F | 1638 |
| Densitylb/cu in. at 68°F | 0.304 |
| Specific Gravity | 8.42 |
| Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 54.9 |
| Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 11.5 |
| Modulus of Elasticity in Tensionksi | 14240 |
| Poisson's Ratio | 0.301 |
| Casting Attribute | Level |
|---|---|
| Casting Yield | High |
| Drossing | Low |
| Fluidity | High |
| Gassing | Low |
| Shrinkage in Solidification | Medium |
| Technique | Suitability |
|---|---|
| Forgeability Rating | 95 |
| Machinability Rating | 85 |
Common Fabrication Processes
No fabrication process properties for this alloy
Thermal Properties
No thermal properties for this alloy
Typical Uses
No information for this alloy
Applicable Specifications
No applicable specifications for this alloy
Corrosion Properties
No Corrosion Properties Available.