C89836
Elements | ||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|
Cu(1) | Pb | Sn | Zn | Fe | P | Ni(2) | Al | Bi | S | Sb | Si | |
(1) Cu + Sum of Named Elements 99.5% min. (2) Ni value includes Co. |
||||||||||||
Min (%) | 87.0 | 4.0 | 2.0 | 1.5 | ||||||||
Max (%) | 91.0 | 0.25 | 7.0 | 4.0 | 0.35 | 0.06 | 0.90 | 0.005 | 3.5 | 0.08 | 0.25 | 0.005 |
Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.5% Ext (ksi) |
Elongation (%) |
Brinell Hardness, 500 kg load |
---|---|---|---|---|---|---|
* Measured at room temperature, 68°F (20°C). | ||||||
As Sand Cast | As Sand Cast | M01 |
33 Min 37.5 Typ |
15 Min 19 Typ |
20 Min 30 Typ |
65 Typ |
Melting Point - Liquidus°F | 1885 |
---|---|
Melting Point - Solidus°F | 1580 |
Densitylb/cu in. at 68°F | 0.318 |
Electrical Conductivity% IACS at 68°F | 18 |
Casting Characteristics
Technique | Suitability |
---|---|
Soldering | Excellent |
Brazing | Good |
Oxyacetylene Welding | Not Recommended |
Gas Shielded Arc Welding | Not Recommended |
Coated Metal Arc Welding | Poor |
Machinability Rating | 85 |
Common Fabrication Processes
Thermal Properties
Product Category | Product | Reason Category | Reason |
---|---|---|---|
Plumbing | Plumbing Castings | Lead Free | Lead Free |
Plumbing Castings | Mechanical Properties | Moderate Strength |
Form | Specific Sub-Form | Application | System | Standard | Description |
---|---|---|---|---|---|
As Sand Cast | ASTM | B584 | COPPER ALLOY SAND CASTINGS FOR GENERAL APPLICATIONS | ||
Ingot | ASTM | B30 | COPPER BASE ALLOYS IN INGOT FORM |
Corrosion Properties