C89837
Elements | ||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|
Cu(1,2) | Pb | Sn | Zn | Fe | P | Ni(3) | Al | Bi | S | Sb | Si | |
(1) 0.01 - 2.0% as any single or combination of Ce La or other rare earth(x) elements as agreed upon. (x)ASM International definition: one of the group of chemically similar metals with atomic numbers 57 through 71 commonly refered to as lanthanides (2) Cu + Sum of Named Elements 99.0% min. (3) Ni value includes Co. |
||||||||||||
Min (%) | 84.0 | 3.0 | 6.0 | 0.7 | ||||||||
Max (%) | 88.0 | 0.10 | 4.0 | 10.0 | 0.30 | 0.050 | 1.0 | 0.005 | 1.2 | 0.08 | 0.25 | 0.005 |
Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.5% Ext (ksi) |
Elongation (%) |
Brinell Hardness, 500 kg load | Izod (ft-lbs) |
---|---|---|---|---|---|---|---|
* Measured at room temperature, 68°F (20°C). | |||||||
As Sand Cast | As Sand Cast | M01 |
37 Typ |
17 Typ |
32 Typ |
60 Typ |
27 Typ |
Melting Point - Liquidus°F | 1854 |
---|---|
Melting Point - Solidus°F | 1472 |
Densitylb/cu in. at 68°F | 0.313 |
Specific Gravity | 8.66 |
Electrical Conductivity% IACS at 68°F | 18 |
Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 39 |
Coefficient of Thermal Expansion 68-39210 to -6 power per °F (68 – 392°F) | 10 |
Specific Heat CapacityBtu/ lb /°F at 68°F | 0.087 |
Modulus of Elasticity in Tensionksi | 13800 |
Casting Attribute | Level |
---|---|
Casting Yield | High |
Drossing | Low |
Effect of Section Size | Low |
Fluidity | High |
Gassing | Medium |
Patternmakers Shrinkage inches per inch | 7/32 |
Shrinkage in Solidification | Low |
Technique | Suitability |
---|---|
Soldering | Excellent |
Brazing | Good |
Oxyacetylene Welding | Not Recommended |
Gas Shielded Arc Welding | Not Recommended |
Coated Metal Arc Welding | Poor |
Machinability Rating | 66 |