C89838
| Elements | |||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| Cu(1) | Pb | Sn | Zn | Fe | P | Ni(2) | Al | Bi | Sb | Si | |
|
(1) Cu + Sum of Named Elements 99.5% min. (2) Ni value includes Co. |
|||||||||||
| Min (%) | 78.0 | 1.5 | 12.0 | 0.20 | |||||||
| Max (%) | 85.0 | 0.09 | 4.0 | 18.0 | 0.30 | 0.05 | 0.50 | 0.01 | 0.9 | 0.05 | 0.01 |
| Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.2% Offset (ksi) |
Elongation (%) |
Brinell Hardness, 500 kg load | Impact Strength (ft-lbs) |
|---|---|---|---|---|---|---|---|
| * Measured at room temperature, 68°F (20°C). | |||||||
| Castings | As Sand Cast | M01 |
28 Min 33 Typ |
10 Min 14 Typ |
15 Min |
59 Min |
18 Min |
| Melting Point - Liquidus°F | 1837 |
|---|---|
| Melting Point - Solidus°F | 1485 |
| Densitylb/cu in. at 68°F | 0.314 |
| Specific Gravity | 8.68 |
| Electrical Conductivity% IACS at 68°F | 21.2 |
| Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 57.8 |
| Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 10.4 |
| Modulus of Elasticity in Tensionksi | 14000 |
| Modulus of Rigidityksi | 5400 |
| Casting Attribute | Level |
|---|---|
| Casting Yield | High |
| Drossing | Medium |
| Effect of Section Size | Medium |
| Fluidity | Medium |
| Gassing | Medium |
| Patternmakers Shrinkage inches per inch | 3/16 |
| Shrinkage in Solidification | Medium |
Fabrication Properties
No fabrication properties for this alloy
Common Fabrication Processes
No fabrication process properties for this alloy
Thermal Properties
No thermal properties for this alloy
Typical Uses
No information for this alloy
Applicable Specifications
No applicable specifications for this alloy
Corrosion Properties
No Corrosion Properties Available.