C90280
| Elements | ||||||
|---|---|---|---|---|---|---|
| Cu(1) | Pb | Sn | Fe | P | S | |
|
(1) Cu + Sum of Named Elements 99.5% min. |
||||||
| Min (%) | 87.0 | 9.0 | .30 | .30 | ||
| Max (%) | 90.0 | .09 | 11.0 | .6 | .05 | .6 |
| Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.2% Offset (ksi) |
Elongation (%) |
|---|---|---|---|---|---|
| * Measured at room temperature, 68°F (20°C). | |||||
| As Die Cast | As Pressure Die Cast | M04 |
315 Typ |
187 Typ |
19.3 Typ |
| As Sand Cast | As Sand Cast | M01 |
315 Typ |
187 Typ |
19.3 Typ |
| Melting Point - Liquidus°F | 1016 |
|---|---|
| Melting Point - Solidus°F | 835 |
| Densitylb/cu in. at 68°F | 8.81 |
| Electrical Conductivity% IACS at 68°F | 0.016 |
| Coefficient of Thermal Expansion 68-21210 to -6 power per °F (68 – 212°F) | 18.3 |
| Coefficient of Thermal Expansion 68-39210 to -6 power per °F (68 – 392°F) | 18.4 |
| Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 18.4 |
Casting Characteristics
No casting characteristics for this alloy
| Technique | Suitability |
|---|---|
| Soldering | Good |
| Brazing | Good |
| Oxyacetylene Welding | Good |
| Gas Shielded Arc Welding | Good |
| Coated Metal Arc Welding | Not Recommended |
| Spot Weld | Good |
| Seam Weld | Not Recommended |
| Butt Weld | Not Recommended |
| Capacity for Being Cold Worked | Not Recommended |
| Capacity for Being Hot Formed | Not Recommended |
| Machinability Rating | 70 |
Common Fabrication Processes
No fabrication process properties for this alloy
Thermal Properties
No thermal properties for this alloy
Typical Uses
No information for this alloy
Applicable Specifications
No applicable specifications for this alloy
Corrosion Properties
No Corrosion Properties Available.