Find suppliers for this alloy C90280
Chemical Composition
Elements
Cu(1) Pb Sn Fe P S
(1) Cu + Sum of Named Elements 99.5% min.
Min (%) 87.0 9.0 .30 .30
Max (%) 90.0 .09 11.0 .6 .05 .6
Mechanical Properties *
Form Temper Temper Code Tensile Strength
(ksi)
YS-0.2% Offset
(ksi)
Elongation
(%)
* Measured at room temperature, 68°F (20°C).
As Die Cast As Pressure Die Cast M04 315 Typ
187 Typ
19.3 Typ
As Sand Cast As Sand Cast M01 315 Typ
187 Typ
19.3 Typ
Physical Properties
Melting Point - Liquidus°F 1016
Melting Point - Solidus°F 835
Densitylb/cu in. at 68°F 8.81
Electrical Conductivity% IACS at 68°F 0.016
Coefficient of Thermal Expansion 68-21210 to -6 power per °F (68 – 212°F) 18.3
Coefficient of Thermal Expansion 68-39210 to -6 power per °F (68 – 392°F) 18.4
Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) 18.4
Casting Characteristics

No casting characteristics for this alloy

Fabrication Properties
Technique Suitability
Soldering Good
Brazing Good
Oxyacetylene Welding Good
Gas Shielded Arc Welding Good
Coated Metal Arc Welding Not Recommended
Spot Weld Good
Seam Weld Not Recommended
Butt Weld Not Recommended
Capacity for Being Cold Worked Not Recommended
Capacity for Being Hot Formed Not Recommended
Machinability Rating 70
Common Fabrication Processes

No fabrication process properties for this alloy

Thermal Properties

No thermal properties for this alloy

Typical Uses

No information for this alloy

Applicable Specifications

No applicable specifications for this alloy

Corrosion Properties

No Corrosion Properties Available.