C90400
Elements | ||||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Cu(1) | Pb | Sn | Zn | Fe | P | Ni | Al | B | Mn | S | Sb | Si | Zr | |
(1) Cu + Sum of Named Elements 99.3% min. |
||||||||||||||
Min (%) | 86.0 | 7.5 | 1.0 | 0.10 | ||||||||||
Max (%) | 89.0 | 0.09 | 8.5 | 5.0 | 0.40 | 0.05 | 1.0 | 0.005 | 0.10 | 0.01 | 0.65 | 0.02 | 0.005 | 0.10 |
Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.5% Ext (ksi) |
Elongation (%) |
Brinell Hardness, 500 kg load |
---|---|---|---|---|---|---|
* Measured at room temperature, 68°F (20°C). | ||||||
Castings | As Sand Cast | M01 |
41.0 Min 45.0 Typ |
22.0 Min 23.5 Typ |
19 Min 27 Typ |
77 Typ |
Melting Point - Liquidus°F | 1810 |
---|---|
Melting Point - Solidus°F | 1566 |
Densitylb/cu in. at 68°F | 0.312 |
Specific Gravity | 8.64 |
Electrical Conductivity% IACS at 68°F | 12 |
Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 43.2 |
Coefficient of Thermal Expansion 68-39210 to -6 power per °F (68 – 392°F) | 10 |
Specific Heat CapacityBtu/ lb /°F at 68°F | 0.087 |
Modulus of Elasticity in Tensionksi | 15300 |
Magnetic Permeability | 1 |
Casting Attribute | Level |
---|---|
Casting Yield | High |
Drossing | Medium |
Effect of Section Size | High |
Fluidity | Medium |
Gassing | Medium |
Patternmakers Shrinkage inches per inch | 3/16 |
Shrinkage in Solidification | Medium |
Fabrication Properties
Common Fabrication Processes
Thermal Properties
Product Category | Product | Reason Category | Reason |
---|---|---|---|
Industrial | Valve Bodies | Corrosion Resistance | Corrosion Resistance |
Valve Bodies | Friction & Wear Properties | Wear Resistance | |
Valve Bodies | Mechanical Properties | Moderate Strength | |
Valve Bodies | Pressure Tight | Pressure Tight up to 260 C |
Applicable Specifications
Corrosion Properties