C90420
Elements | ||||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Cu(1) | Pb | Sn | Zn | Fe | P | Ni | B | C | Mn | S | Sb | Ti | Zr | |
(1) Cu + Sum of Named Elements 99.3% min. |
||||||||||||||
Min (%) | 86.0 | 7.5 | 1.0 | 0.10 | ||||||||||
Max (%) | 89.0 | 0.09 | 8.5 | 5.0 | 0.40 | 0.05 | 1.0 | 0.10 | 0.10 | 0.20 | 0.65 | 0.02 | 0.10 | 0.10 |
Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.5% Ext (ksi) |
Elongation (%) |
Brinell Hardness, 500 kg load |
---|---|---|---|---|---|---|
* Measured at room temperature, 68°F (20°C). | ||||||
Castings | As Sand Cast | M01 |
41 Min 45 Typ |
22 Min 24 Typ |
17 Min 23 Typ |
76 Typ |
Melting Point - Liquidus°F | 1865 |
---|---|
Melting Point - Solidus°F | 1535 |
Densitylb/cu in. at 68°F | 0.312 |
Specific Gravity | 8.64 |
Electrical Conductivity% IACS at 68°F | 12 |
Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 43.2 |
Coefficient of Thermal Expansion 68-39210 to -6 power per °F (68 – 392°F) | 10 |
Specific Heat CapacityBtu/ lb /°F at 68°F | 0.07 |
Modulus of Elasticity in Tensionksi | 15600 |
Magnetic Permeability | 1 |
Casting Attribute | Level |
---|---|
Casting Yield | High |
Drossing | Medium |
Effect of Section Size | High |
Fluidity | Medium |
Gassing | Medium |
Patternmakers Shrinkage inches per inch | 3/16 |
Shrinkage in Solidification | Medium |
Fabrication Properties
Common Fabrication Processes
Thermal Properties
Typical Uses
Form | Specific Sub-Form | Application | System | Standard | Description |
---|---|---|---|---|---|
As Sand Cast | ASTM | B584 | COPPER ALLOY SAND CASTINGS FOR GENERAL APPLICATIONS | ||
Ingot | ASTM | B30 | COPPER BASE ALLOYS IN INGOT FORM |
Corrosion Properties