C90500
| Elements | |||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| Cu(1,2) | Pb | Sn | Zn | Fe | P(3) | Ni(4) | Al | S | Sb | Si | |
|
(1) Cu + Sum of Named Elements 99.7% min. (2) In determining Cu min., Cu may be calculated as Cu + Ni. (3) For continuous castings P shall be 1.5% max. (4) Ni value includes Co. |
|||||||||||
| Min (%) | 86.0 | 9.0 | 1.0 | ||||||||
| Max (%) | 89.0 | 0.30 | 11.0 | 3.0 | 0.20 | 0.05 | 1.0 | 0.005 | 0.05 | 0.20 | 0.005 |
| Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.5% Ext (ksi) |
Elongation (%) |
Brinell Hardness, 500 kg load | Izod (ft-lbs) |
Compressive Strength .01 in. set/in. (ksi) |
Fatigue Strength** (ksi) |
Reduction of Area (%) |
|---|---|---|---|---|---|---|---|---|---|---|
| * Measured at room temperature, 68°F (20°C). ** Fatigue Strength: 100 x 106 cycles, unless indicated as [N] x 106. | ||||||||||
| As Centrifugal Cast | As Centrifugal Cast | M02 |
40 Min for Standard 40 Min for Standard 45 Typ |
18 Min for Standard 22 Typ |
20 Min for Standard 20 Min for Standard 25 Typ |
75 Typ |
10 Typ | 40 Typ | 13 Typ | |
| As Continuous Cast | As Continuous Cast | M07 |
44 Min for Standard 44 Min for Standard |
25 Min for Standard |
10 Min for Standard 10 Min for Standard |
|||||
| As Sand Cast | As Sand Cast | M01 |
40 Min for Standard 40 Min for Standard 45 Typ |
18 Min for Standard 22 Typ |
20 Min for Standard 20 Min for Standard 25 Typ |
75 Typ |
10 Typ | 40 Typ | 13 Typ | 40 Typ |
| Melting Point - Liquidus°F | 1830 |
|---|---|
| Melting Point - Solidus°F | 1570 |
| Densitylb/cu in. at 68°F | 0.315 |
| Specific Gravity | 8.72 |
| Electrical Conductivity% IACS at 68°F | 11 |
| Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 43.2 |
| Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 11 |
| Specific Heat CapacityBtu/ lb /°F at 68°F | 0.09 |
| Modulus of Elasticity in Tensionksi | 15000 |
| Magnetic Permeability | 1 |
| Casting Attribute | Level |
|---|---|
| Casting Yield | Medium |
| Drossing | Low |
| Effect of Section Size | High |
| Fluidity | Medium |
| Gassing | Medium |
| Patternmakers Shrinkage inches per inch | 3/16 |
| Shrinkage in Solidification | Medium |
| Technique | Suitability |
|---|---|
| Soldering | Excellent |
| Brazing | Good |
| Oxyacetylene Welding | Fair |
| Gas Shielded Arc Welding | Fair |
| Coated Metal Arc Welding | Fair |
| Machinability Rating | 30 |
Common Fabrication Processes
No fabrication process properties for this alloy
| Treatment | Value* | Time** | ||
|---|---|---|---|---|
| * Temperature is measured in Fahrenheit. ** Time is measured in minutes. | ||||
| Stress Relief | 500 | |||
| Solution Treatment | 0 | |||
| Product Category | Product | Reason Category | Reason |
|---|---|---|---|
| Builders Hardware | Clamps | Corrosion Resistance | Corrosion Resistance |
| Clamps | Corrosion Resistance | Corrosion Resistance to Numerous Environments | |
| Clamps | Mechanical Properties | Moderate Strength | |
| Building | Heavy Construction Equipment | Corrosion Resistance | Corrosion Resistance |
| Heavy Construction Equipment | Friction & Wear Properties | Wear Resistance | |
| Heavy Construction Equipment | Mechanical Properties | Moderate Strength | |
| Heavy Construction Equipment | Pressure Tight | Pressure Tight up to 260 C | |
| Electrical | Connectors | Conductivity (Electrical) | Electrical Conductivity |
| Connectors | Conductivity (Thermal) | Thermal Conductivity | |
| Connectors | Corrosion Resistance | Corrosion Resistance | |
| Connectors | Corrosion Resistance | Corrosion Resistance to Numerous Environments | |
| Connectors | Mechanical Properties | Moderate Strength | |
| Fasteners | Nuts | Corrosion Resistance | Corrosion Resistance |
| Nuts | Mechanical Properties | Moderate Strength | |
| Industrial | Bearings | Corrosion Resistance | Corrosion Resistance |
| Bearings | Friction & Wear Properties | Low Co-efficient of Friction | |
| Bearings | Friction & Wear Properties | Wear Resistance | |
| Bearings | Mechanical Properties | Moderate Strength | |
| Bushings | Corrosion Resistance | Corrosion Resistance | |
| Bushings | Friction & Wear Properties | Low Co-efficient of Friction | |
| Bushings | Friction & Wear Properties | Wear Resistance | |
| Bushings | Mechanical Properties | Moderate Strength | |
| Expansion Bearings | Corrosion Resistance | Corrosion Resistance | |
| Expansion Bearings | Friction & Wear Properties | Wear Resistance | |
| Expansion Bearings | Mechanical Properties | Moderate Strength | |
| Finishing Dies for Wood Pulp Industry | Corrosion Resistance | Corrosion Resistance | |
| Finishing Dies for Wood Pulp Industry | Corrosion Resistance | Corrosion Resistance to Fresh Water | |
| Finishing Dies for Wood Pulp Industry | Corrosion Resistance | Corrosion Resistance to Numerous Environments | |
| Finishing Dies for Wood Pulp Industry | Corrosion Resistance | Corrosion Resistance to Saline Solutions | |
| Finishing Dies for Wood Pulp Industry | Friction & Wear Properties | Wear Resistance | |
| Finishing Dies for Wood Pulp Industry | Mechanical Properties | Moderate Strength | |
| Finishing Dies for Wood Pulp Industry | Pressure Tight | Pressure Tight up to 260 C | |
| Gear Blanks | Corrosion Resistance | Corrosion Resistance | |
| Gear Blanks | Friction & Wear Properties | Wear Resistance | |
| Gear Blanks | Machining Properties | Machinability, Good | |
| Gear Blanks | Mechanical Properties | Moderate Strength | |
| Gears | Corrosion Resistance | Corrosion Resistance | |
| Gears | Friction & Wear Properties | Low Co-efficient of Friction | |
| Gears | Friction & Wear Properties | Wear Resistance | |
| Gears | Machining Properties | Machinability, Good | |
| Gears | Mechanical Properties | Moderate Strength | |
| Piston Rings | Corrosion Resistance | Corrosion Resistance | |
| Piston Rings | Friction & Wear Properties | Wear Resistance | |
| Piston Rings | Mechanical Properties | Moderate Strength | |
| Piston Rings | Pressure Tight | Pressure Tight up to 260 C | |
| Pump Bodies | Corrosion Resistance | Corrosion Resistance | |
| Pump Bodies | Corrosion Resistance | Corrosion Resistance to Fresh Water | |
| Pump Bodies | Corrosion Resistance | Corrosion Resistance to Numerous Environments | |
| Pump Bodies | Corrosion Resistance | Corrosion Resistance to Saline Solutions | |
| Pump Bodies | Mechanical Properties | Moderate Strength | |
| Pump Bodies | Pressure Tight | Pressure Tight up to 260 C | |
| Pump Impellers | Corrosion Resistance | Corrosion Resistance | |
| Pump Impellers | Corrosion Resistance | Corrosion Resistance to Fresh Water | |
| Pump Impellers | Corrosion Resistance | Corrosion Resistance to Numerous Environments | |
| Pump Impellers | Corrosion Resistance | Corrosion Resistance to Saline Solutions | |
| Pump Impellers | Friction & Wear Properties | Wear Resistance | |
| Pump Impellers | Mechanical Properties | Moderate Strength | |
| Pump Impellers | Pressure Tight | Pressure Tight up to 260 C | |
| Seal Rings | Corrosion Resistance | Corrosion Resistance | |
| Seal Rings | Friction & Wear Properties | Wear Resistance | |
| Seal Rings | Mechanical Properties | Moderate Strength | |
| Valve Bodies | Corrosion Resistance | Corrosion Resistance | |
| Valve Bodies | Friction & Wear Properties | Wear Resistance | |
| Valve Bodies | Mechanical Properties | Moderate Strength | |
| Valve Bodies | Pressure Tight | Pressure Tight up to 260 C | |
| Valves | Corrosion Resistance | Corrosion Resistance | |
| Valves | Friction & Wear Properties | Wear Resistance | |
| Valves | Mechanical Properties | Moderate Strength | |
| Worm Gears | Corrosion Resistance | Corrosion Resistance | |
| Worm Gears | Friction & Wear Properties | Wear Resistance | |
| Worm Gears | Mechanical Properties | Moderate Strength | |
| Plumbing | Steam Fittings | Corrosion Resistance | Corrosion Resistance |
| Steam Fittings | Corrosion Resistance | Corrosion Resistance to Numerous Environments | |
| Steam Fittings | Mechanical Properties | Moderate Strength | |
| Steam Fittings | Pressure Tight | Pressure Tight up to 260 C | |
| Water Conditioners | Corrosion Resistance | Corrosion Resistance | |
| Water Conditioners | Corrosion Resistance | Corrosion Resistance to Fresh Water | |
| Water Conditioners | Corrosion Resistance | Corrosion Resistance to Saline Solutions | |
| Water Conditioners | Mechanical Properties | Moderate Strength |
| Form | Specific Sub-Form | Application | System | Standard | Description |
|---|---|---|---|---|---|
| As Centrifugal Cast | Castings | ASTM | B271/B271M | COPPER BASE ALLOY CENTRIFUGAL CASTINGS | |
| Castings | SAE | J462 | CAST COPPER ALLOYS | ||
| Castings | AMS | 4845 | TIN BRONZE CASTINGS, SAND AND CENTRIFUGAL, AS CAST | ||
| Castings | SAE | J461 | WROUGHT AND CAST COPPER ALLOYS | ||
| As Continuous Cast | Castings | SAE | J461 | WROUGHT AND CAST COPPER ALLOYS | |
| Castings | SAE | J462 | CAST COPPER ALLOYS | ||
| Castings | ASTM | B505/B505M | COPPER BASE ALLOY CONTINUOUS CASTINGS | ||
| As Sand Cast | Castings | SAE | J461 | WROUGHT AND CAST COPPER ALLOYS | |
| Castings | AMS | 4845 | TIN BRONZE CASTINGS, SAND AND CENTRIFUGAL, AS CAST | ||
| Castings | SAE | J462 | CAST COPPER ALLOYS | ||
| Castings | ASTM | B584 | COPPER ALLOY SAND CASTINGS FOR GENERAL APPLICATIONS | ||
| Castings | ASTM | B22/B22M | BRONZE CASTINGS FOR BRIDGES AND TURNTABLES | ||
| Castings | ASTM | B763/B763M | COPPER ALLOY SAND CASTINGS FOR VALVE APPLICATIONS | ||
| Ingot | ASTM | B30 | COPPER BASE ALLOYS IN INGOT FORM | ||
Corrosion Properties
No Corrosion Properties Available.