Find suppliers for this alloy
C91000
Elements | |||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|
Cu(1,2) | Pb | Sn | Zn | Fe | P(3) | Ni(4) | Al | S | Sb | Si | |
(1) Cu + Sum of Named Elements 99.4% min. (2) In determining Cu min., Cu may be calculated as Cu + Ni. (3) For continuous castings P shall be 1.5% max. (4) Ni value includes Co. |
|||||||||||
Min (%) | 84.0 | 14.0 | |||||||||
Max (%) | 86.0 | 0.20 | 16.0 | 1.5 | 0.10 | 0.05 | 0.8 | 0.005 | 0.05 | 0.20 | 0.005 |
Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.5% Ext (ksi) |
Elongation (%) |
Brinell Hardness, 500 kg load |
---|---|---|---|---|---|---|
* Measured at room temperature, 68°F (20°C). | ||||||
As Continuous Cast | As Continuous Cast | M07 |
30 Min for Standard |
|||
As Sand Cast | As Sand Cast | M01 |
32 Typ |
25 Typ |
2 Typ |
105 Typ |
Melting Point - Liquidus°F | 1760 |
---|---|
Melting Point - Solidus°F | 1505 |
Electrical Conductivity% IACS at 68°F | 9 |
Specific Heat CapacityBtu/ lb /°F at 68°F | 0.09 |
Modulus of Elasticity in Tensionksi | 16000 |
Casting Attribute | Level |
---|---|
Casting Yield | Medium |
Drossing | Low |
Effect of Section Size | High |
Fluidity | High |
Gassing | Medium |
Patternmakers Shrinkage inches per inch | 3/16 |
Shrinkage in Solidification | Low |
Technique | Suitability |
---|---|
Soldering | Excellent |
Brazing | Good |
Oxyacetylene Welding | Fair |
Gas Shielded Arc Welding | Fair |
Coated Metal Arc Welding | Fair |
Machinability Rating | 20 |
Common Fabrication Processes
Treatment | Value* | Time** | ||
---|---|---|---|---|
* Temperature is measured in Fahrenheit. ** Time is measured in minutes. | ||||
Stress Relief | 500 | |||
Solution Treatment | 0 |
Product Category | Product | Reason Category | Reason |
---|---|---|---|
Industrial | Bearings | Corrosion Resistance | Corrosion Resistance |
Bearings | Friction & Wear Properties | Anti-Seizing Properties | |
Bearings | Friction & Wear Properties | Low Co-efficient of Friction | |
Bearings | Friction & Wear Properties | Wear Resistance | |
Bearings | Mechanical Properties | Moderate Strength | |
Piston Rings | Corrosion Resistance | Corrosion Resistance | |
Piston Rings | Friction & Wear Properties | Wear Resistance | |
Piston Rings | Mechanical Properties | Moderate Strength | |
Piston Rings | Pressure Tight | Pressure Tight up to 260 C |
Form | Specific Sub-Form | Application | System | Standard | Description |
---|---|---|---|---|---|
As Continuous Cast | Castings | ASTM | B505/B505M | COPPER BASE ALLOY CONTINUOUS CASTINGS | |
Ingot | |||||
ASTM | B30 | COPPER BASE ALLOYS IN INGOT FORM |
Corrosion Properties