C91100
| Elements | |||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| Cu(1,2) | Pb | Sn | Zn | Fe | P(3) | Ni(4) | Al | S | Sb | Si | |
|
(1) In determining Cu min., Cu may be calculated as Cu + Ni. (2) Cu + Sum of Named Elements 99.4% min. (3) For continuous castings P shall be 1.5% max. (4) Ni value includes Co. |
|||||||||||
| Min (%) | 82.0 | 15.0 | |||||||||
| Max (%) | 85.0 | 0.25 | 17.0 | 0.25 | 0.25 | 1.0 | 0.50 | 0.005 | 0.05 | 0.20 | 0.005 |
| Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.5% Ext (ksi) |
Elongation (%) |
Brinell Hardness, 3000 kg load | Proportional Limit (ksi) |
|---|---|---|---|---|---|---|---|
| * Measured at room temperature, 68°F (20°C). | |||||||
| As Sand Cast | As Sand Cast | M01 |
35 Typ |
25 Typ |
2 Typ |
135 Typ |
16 Typ |
| Melting Point - Liquidus°F | 1742 |
|---|---|
| Melting Point - Solidus°F | 1505 |
| Electrical Conductivity% IACS at 68°F | 8 |
| Specific Heat CapacityBtu/ lb /°F at 68°F | 0.09 |
| Modulus of Elasticity in Tensionksi | 15000 |
| Casting Attribute | Level |
|---|---|
| Casting Yield | Medium |
| Drossing | Low |
| Effect of Section Size | Medium |
| Fluidity | High |
| Gassing | Med-High |
| Patternmakers Shrinkage inches per inch | 3/16 |
| Shrinkage in Solidification | Low |
| Technique | Suitability |
|---|---|
| Soldering | Excellent |
| Brazing | Good |
| Oxyacetylene Welding | Fair |
| Gas Shielded Arc Welding | Fair |
| Coated Metal Arc Welding | Fair |
| Machinability Rating | 10 |
Common Fabrication Processes
No fabrication process properties for this alloy
| Treatment | Value* | Time** | ||
|---|---|---|---|---|
| * Temperature is measured in Fahrenheit. ** Time is measured in minutes. | ||||
| Stress Relief | 500 | |||
| Solution Treatment | 0 | |||
| Product Category | Product | Reason Category | Reason |
|---|---|---|---|
| Electrical | Hollow Conductors | Conductivity (Electrical) | Electrical Conductivity |
| Hollow Conductors | Conductivity (Electrical) | High Electrical Conductivity at Elevated Temperatures | |
| Hollow Conductors | Conductivity (Thermal) | Thermal Conductivity | |
| Hollow Conductors | Corrosion Resistance | Corrosion Resistance | |
| Hollow Conductors | Mechanical Properties | Moderate Strength | |
| Industrial | Bearings | Corrosion Resistance | Corrosion Resistance |
| Bearings | Corrosion Resistance | Corrosion Resistance to Numerous Environments | |
| Bearings | Friction & Wear Properties | Wear Resistance | |
| Bearings | Mechanical Properties | Moderate Strength | |
| Bushings | Corrosion Resistance | Corrosion Resistance | |
| Bushings | Corrosion Resistance | Corrosion Resistance to Numerous Environments | |
| Bushings | Friction & Wear Properties | Wear Resistance | |
| Bushings | Mechanical Properties | Moderate Strength | |
| Piston Rings | Corrosion Resistance | Corrosion Resistance | |
| Piston Rings | Corrosion Resistance | Corrosion Resistance to Numerous Environments | |
| Piston Rings | Friction & Wear Properties | Wear Resistance | |
| Piston Rings | Mechanical Properties | Moderate Strength |
| Form | Specific Sub-Form | Application | System | Standard | Description |
|---|---|---|---|---|---|
| As Sand Cast | Castings | ASTM | B22/B22M | BRONZE CASTINGS FOR BRIDGES AND TURNTABLES | |
| Ingot | ASTM | B30 | COPPER BASE ALLOYS IN INGOT FORM |
Corrosion Properties
No Corrosion Properties Available.