C92800
Elements | |||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|
Cu(1,2) | Pb | Sn | Zn | Fe | P(3) | Ni(4) | Al | S | Sb | Si | |
(1) Cu + Sum of Named Elements 99.3% min. (2) In determining Cu min., Cu may be calculated as Cu + Ni. (3) For continuous castings P shall be 1.5% max. (4) Ni value includes Co. |
|||||||||||
Min (%) | 78.0 | 4.0 | 15.0 | ||||||||
Max (%) | 82.0 | 6.0 | 17.0 | 0.8 | 0.20 | 0.05 | 0.8 | 0.005 | 0.05 | 0.25 | 0.005 |
Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.5% Ext (ksi) |
Elongation (%) |
Rockwell B scale |
---|---|---|---|---|---|---|
* Measured at room temperature, 68°F (20°C). | ||||||
As Continuous Cast | As Continuous Cast | M07 | ||||
As Sand Cast | As Sand Cast | M01 |
40 Typ |
30 Typ |
1 Typ |
80 Typ |
Melting Point - Liquidus°F | 1751 |
---|---|
Melting Point - Solidus°F | 1505 |
Specific Heat CapacityBtu/ lb /°F at 68°F | 0.09 |
Modulus of Elasticity in Tensionksi | 16000 |
Casting Attribute | Level |
---|---|
Casting Yield | Medium |
Drossing | Low |
Effect of Section Size | Medium |
Fluidity | Medium |
Gassing | Medium |
Patternmakers Shrinkage inches per inch | 3/16 |
Shrinkage in Solidification | Low |
Technique | Suitability |
---|---|
Soldering | Excellent |
Brazing | Good |
Oxyacetylene Welding | Not Recommended |
Gas Shielded Arc Welding | Not Recommended |
Coated Metal Arc Welding | Not Recommended |
Machinability Rating | 70 |
Common Fabrication Processes
Treatment | Value* | Time** | ||
---|---|---|---|---|
* Temperature is measured in Fahrenheit. ** Time is measured in minutes. | ||||
Stress Relief | 500 | |||
Solution Treatment | 0 |
Product Category | Product | Reason Category | Reason |
---|---|---|---|
Industrial | Bushings | Corrosion Resistance | Corrosion Resistance |
Bushings | Corrosion Resistance | Corrosion Resistance to Numerous Environments | |
Bushings | Friction & Wear Properties | Anti-Seizing Properties | |
Bushings | Friction & Wear Properties | Low Coefficient of Friction | |
Bushings | Friction & Wear Properties | Wear Resistance | |
Bushings | Machining Properties | Machinability, Good | |
Bushings | Mechanical Properties | Moderate Strength | |
Corrosion Resistant Castings | Corrosion Resistance | Corrosion Resistance | |
Corrosion Resistant Castings | Corrosion Resistance | Corrosion Resistance to Brackish Water | |
Corrosion Resistant Castings | Corrosion Resistance | Corrosion Resistance to Numerous Environments | |
Corrosion Resistant Castings | Corrosion Resistance | Corrosion Resistance to Petroleum Products | |
Corrosion Resistant Castings | Friction & Wear Properties | Wear Resistance | |
Corrosion Resistant Castings | Machining Properties | Machinability, Good | |
Corrosion Resistant Castings | Mechanical Properties | Moderate Strength | |
Piston Rings | Corrosion Resistance | Corrosion Resistance | |
Piston Rings | Corrosion Resistance | Corrosion Resistance to Numerous Environments | |
Piston Rings | Friction & Wear Properties | Wear Resistance | |
Piston Rings | Machining Properties | Machinability, Good | |
Piston Rings | Mechanical Properties | Moderate Strength |
Form | Specific Sub-Form | Application | System | Standard | Description |
---|---|---|---|---|---|
As Continuous Cast | Castings | ASTM | B505/B505M | COPPER BASE ALLOY CONTINUOUS CASTINGS | |
Ingot | ASTM | B30 | COPPER BASE ALLOYS IN INGOT FORM |
Corrosion Properties