C94500
Elements | |||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|
Cu(1) | Pb | Sn | Zn | Fe | P(2) | Ni(3) | Al | S | Sb | Si | |
(1) Cu + Sum of Named Elements 99.0% min. (2) For continuous castings P shall be 1.5% max. (3) Ni value includes Co. |
|||||||||||
Min (%) | 16.0 | 6.0 | |||||||||
Max (%) | Rem | 22.0 | 8.0 | 1.2 | 0.15 | 0.05 | 1.0 | 0.005 | 0.08 | 0.8 | 0.005 |
Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.5% Ext (ksi) |
Elongation (%) |
Brinell Hardness, 500 kg load | Shear Strength (ksi) |
Izod (ft-lbs) |
Compressive Strength .1 in. set/in. (ksi) |
Fatigue Strength** (ksi) |
Proportional Limit (ksi) |
---|---|---|---|---|---|---|---|---|---|---|---|
* Measured at room temperature, 68°F (20°C). ** Fatigue Strength: 100 x 106 cycles, unless indicated as [N] x 106. | |||||||||||
As Sand Cast | As Sand Cast | M01 |
25 Typ |
12 Typ |
12 Typ |
50 Typ |
13 Typ |
4 Typ | 36 Typ | 10 Typ | 4 Typ |
Melting Point - Liquidus°F | 1725 |
---|---|
Melting Point - Solidus°F | 1475 |
Densitylb/cu in. at 68°F | 0.34 |
Specific Gravity | 9.41 |
Electrical Conductivity% IACS at 68°F | 10 |
Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 30.2 |
Coefficient of Thermal Expansion 68-39210 to -6 power per °F (68 – 392°F) | 10.3 |
Specific Heat CapacityBtu/ lb /°F at 68°F | 0.09 |
Modulus of Elasticity in Tensionksi | 10500 |
Incipient Melting°F | 600 |
Magnetic Permeability | 1 |
Casting Attribute | Level |
---|---|
Casting Yield | High |
Drossing | Low |
Effect of Section Size | Low |
Fluidity | High |
Gassing | Medium |
Patternmakers Shrinkage inches per inch | 2/16 |
Shrinkage in Solidification | Low |
Technique | Suitability |
---|---|
Soldering | Good |
Brazing | Poor |
Oxyacetylene Welding | Not Recommended |
Gas Shielded Arc Welding | Not Recommended |
Coated Metal Arc Welding | Not Recommended |
Machinability Rating | 80 |
Common Fabrication Processes
Treatment | Value* | Time** | ||
---|---|---|---|---|
* Temperature is measured in Fahrenheit. ** Time is measured in minutes. | ||||
Stress Relief | 500 | |||
Solution Treatment | 0 |
Product Category | Product | Reason Category | Reason |
---|---|---|---|
Industrial | Corrosion Resistant Castings | Corrosion Resistance | Corrosion Resistance |
Corrosion Resistant Castings | Corrosion Resistance | Corrosion Resistance to Brackish Water | |
Corrosion Resistant Castings | Corrosion Resistance | Corrosion Resistance to Many Industrial Chemicals | |
Corrosion Resistant Castings | Corrosion Resistance | Corrosion Resistance to Numerous Environments | |
Corrosion Resistant Castings | Friction & Wear Properties | Wear Resistance | |
High Load, Low Speed Bearings | Corrosion Resistance | Corrosion Resistance | |
High Load, Low Speed Bearings | Corrosion Resistance | Corrosion Resistance to Numerous Environments | |
High Load, Low Speed Bearings | Friction & Wear Properties | Wear Resistance | |
High Load, Low Speed Bearings | Machining Characteristics | Excellent Machinability | |
Locomotive Shoes | Conductivity (Thermal) | Thermal Conductivity | |
Locomotive Shoes | Corrosion Resistance | Corrosion Resistance | |
Locomotive Shoes | Corrosion Resistance | Corrosion Resistance to Numerous Environments | |
Locomotive Shoes | Friction & Wear Properties | Wear Resistance | |
Locomotive Wedges | Conductivity (Thermal) | Thermal Conductivity | |
Locomotive Wedges | Corrosion Resistance | Corrosion Resistance | |
Locomotive Wedges | Corrosion Resistance | Corrosion Resistance to Numerous Environments | |
Locomotive Wedges | Friction & Wear Properties | Wear Resistance |
Form | Specific Sub-Form | Application | System | Standard | Description |
---|---|---|---|---|---|
As Sand Cast | Castings | ASTM | B66 | BRONZE CASTINGS IN THE ROUGH FOR LOCOMOTIVE WEARING PARTS | |
Ingot | AMS | 4500 | COPPER SHEET, STRIP AND PLATE, SOFT ANNEALED | ||
ASTM | B30 | COPPER BASE ALLOYS IN INGOT FORM |
Corrosion Properties