Find suppliers for this alloy
C95300
Elements | |||
---|---|---|---|
Cu(1) | Fe | Al | |
(1) Cu + Sum of Named Elements 99.0% min. |
|||
Min (%) | 86.0 | 0.8 | 9.0 |
Max (%) | 1.5 | 11.0 |
Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.5% Ext (ksi) |
Elongation (%) |
Rockwell B scale | Brinell Hardness, 3000 kg load | Shear Strength (ksi) |
Izod (ft-lbs) |
Charpy V-Notch Impact Strength (ft-lbs) |
Compressive Strength .001 in. set/in. (ksi) |
Compressive Strength .1 in. set/in. (ksi) |
Fatigue Strength** (ksi) |
Proportional Limit (ksi) |
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
* Measured at room temperature, 68°F (20°C). ** Fatigue Strength: 100 x 106 cycles, unless indicated as [N] x 106. | ||||||||||||||
As Centrifugal Cast | As Centrifugal Cast | M02 |
65 Min for Standard 65 Min for Standard |
25 Min for Standard |
20 Min for Standard 20 Min for Standard |
110 Min for Standard |
||||||||
Quenched Hardened and Temper Annealed | TQ50 |
80 Min for Standard 80 Min for Standard |
12 Min for Standard 12 Min for Standard |
160 Min for Standard |
||||||||||
As Continuous Cast | As Continuous Cast | M07 |
70 Min for Standard 70 Min for Standard |
26 Min for Standard |
25 Min for Standard 25 Min for Standard |
|||||||||
Quenched Hardened and Temper Annealed | TQ50 |
80 Min for Standard 80 Min for Standard |
12 Min for Standard 12 Min for Standard |
|||||||||||
As Permanent Mold Cast | As Permanent Mold Cast | M05 |
80 Min for Standard |
30 Min for Standard |
20 Min for Standard |
|||||||||
As Sand Cast | As Sand Cast | M01 |
65 Min for Standard 65 Min for Standard 75 Typ |
25 Min for Standard 27 Typ |
20 Min for Standard 20 Min for Standard 25 Typ |
67 Typ |
110 Min for Standard 140 Typ |
41 Typ |
28 Typ | 23 Typ |
20 Typ | 83 Typ | 22 Typ | 15 Typ |
Quenched Hardened and Temper Annealed | TQ50 |
90 Min for Standard 80 Min for Standard 85 Typ |
42 Typ |
12 Min for Standard 12 Min for Standard 15 Typ |
81 Typ |
160 Min for Standard 174 Typ |
46 Typ |
27 Typ | 35 Typ | 90 Typ | 27 Typ | 26 Typ |
(1)Field Strength 8 kA/m | |
Melting Point - Liquidus°F | 1913 |
---|---|
Melting Point - Solidus°F | 1904 |
Densitylb/cu in. at 68°F | 0.272 |
Specific Gravity | 7.53 |
Electrical Conductivity% IACS at 68°F | 13 |
Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 36.3 |
Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 9 |
Specific Heat CapacityBtu/ lb /°F at 68°F | 0.09 |
Modulus of Elasticity in Tensionksi | 16000 |
Magnetic Permeability | 1.07 (1) |
Casting Attribute | Level |
---|---|
Casting Yield | Low |
Drossing | High |
Effect of Section Size | Low |
Fluidity | Medium |
Gassing | Medium |
Patternmakers Shrinkage inches per inch | 3/16 |
Shrinkage in Solidification | High |
Technique | Suitability |
---|---|
Soldering | Good |
Brazing | Good |
Oxyacetylene Welding | Not Recommended |
Gas Shielded Arc Welding | Excellent |
Coated Metal Arc Welding | Good |
Machinability Rating | 55 |
Common Fabrication Processes
Treatment | Minimum* | Maximum* | Value* | Time** | Medium |
---|---|---|---|---|---|
* Temperature is measured in Fahrenheit. ** Time is measured in minutes. | |||||
Stress Relief | 600 | ||||
Solution Treatment | 1585 | 1635 | 1 | Water | |
Annealing | 1150 | 1225 | 1 |
Product Category | Product | Reason Category | Reason |
---|---|---|---|
Electrical | Connectors | Conductivity (Electrical) | Electrical Conductivity |
Connectors | Conductivity (Thermal) | Thermal Conductivity | |
Connectors | Corrosion Resistance | Corrosion Resistance (Excellent) | |
Connectors | Mechanical Properties | High Strength | |
Fasteners | Stripped Nuts | Corrosion Resistance | Corrosion Resistance (Excellent) |
Stripped Nuts | Mechanical Properties | High Strength | |
Industrial | Bearing Segment for the Steel Industry | Corrosion Resistance | Corrosion Resistance (Excellent) |
Bearing Segment for the Steel Industry | Friction & Wear Properties | Wear Resistance | |
Bearing Segment for the Steel Industry | Mechanical Properties | High Strength | |
Bearing Segment for the Steel Industry | Mechanical Properties | Retains Strength at Elevated Temperatures | |
Cams | Corrosion Resistance | Corrosion Resistance | |
Cams | Friction & Wear Properties | Wear Resistance | |
Cams | Mechanical Properties | High Strength | |
Gears | Corrosion Resistance | Corrosion Resistance (Excellent) | |
Gears | Friction & Wear Properties | Wear Resistance | |
Gears | Machining Properties | Machinability, Good | |
Gears | Mechanical Properties | High Strength | |
High Strength Clamps | Corrosion Resistance | Corrosion Resistance (Excellent) | |
High Strength Clamps | Mechanical Properties | High Strength | |
High Temperature Applications | Corrosion Resistance | Corrosion Resistance (Excellent) | |
High Temperature Applications | Friction & Wear Properties | Wear Resistance | |
High Temperature Applications | Mechanical Properties | High Strength | |
High Temperature Applications | Mechanical Properties | Retains Strength at Elevated Temperatures | |
Large Hold Down Screws | Corrosion Resistance | Corrosion Resistance (Excellent) | |
Large Hold Down Screws | Machining Properties | Machinability, Good | |
Large Hold Down Screws | Mechanical Properties | High Strength | |
Mining Machine Parts | Corrosion Resistance | Corrosion Resistance (Excellent) | |
Mining Machine Parts | Friction & Wear Properties | Wear Resistance | |
Mining Machine Parts | Mechanical Properties | High Strength | |
Mining Machine Parts | Mechanical Properties | Retains Strength at Elevated Temperatures | |
Pickling Baskets | Corrosion Resistance | Corrosion Resistance | |
Pickling Baskets | Corrosion Resistance | Corrosion Resistance to Acids | |
Pickling Baskets | Mechanical Properties | High Strength | |
Pickling Baskets | Mechanical Properties | Retains Strength at Elevated Temperatures | |
Pickling Hooks | Corrosion Resistance | Corrosion Resistance | |
Pickling Hooks | Corrosion Resistance | Corrosion Resistance to Acids | |
Pickling Hooks | Mechanical Properties | High Strength | |
Pickling Hooks | Mechanical Properties | Retains Strength at Elevated Temperatures | |
Pressure Blocks for the Steel Industry | Corrosion Resistance | Corrosion Resistance (Excellent) | |
Pressure Blocks for the Steel Industry | Friction & Wear Properties | Wear Resistance | |
Pressure Blocks for the Steel Industry | Mechanical Properties | High Strength | |
Pressure Blocks for the Steel Industry | Mechanical Properties | Retains Strength at Elevated Temperatures | |
Valve Bodies | Corrosion Resistance | Corrosion Resistance (Excellent) | |
Valve Bodies | Friction & Wear Properties | Wear Resistance | |
Valve Bodies | Machining Properties | Machinability, Good | |
Valve Bodies | Mechanical Properties | High Strength | |
Welding Jaws | Corrosion Resistance | Corrosion Resistance | |
Welding Jaws | Corrosion Resistance | Oxidation Resistance | |
Welding Jaws | Mechanical Properties | High Strength | |
Welding Jaws | Mechanical Properties | Retains Strength at Elevated Temperatures | |
Marine | Covers for Marine Hardware | Appearance | Appearance |
Covers for Marine Hardware | Corrosion Resistance | Corrosion Resistance (Excellent) | |
Covers for Marine Hardware | Corrosion Resistance | Corrosion Resistance to Salt Water | |
Covers for Marine Hardware | Mechanical Properties | High Strength | |
Marine Equipment | Corrosion Resistance | Corrosion Resistance | |
Marine Equipment | Corrosion Resistance | Corrosion Resistance to Salt Water | |
Marine Equipment | Mechanical Properties | High Strength | |
Marine Equipment | Mechanical Properties | Retains Strength at Elevated Temperatures |
Applicable Specifications