C95600
| Elements | ||||
|---|---|---|---|---|
| Cu(1) | Ni(2) | Al | Si | |
|
(1) Cu + Sum of Named Elements 99.0% min. (2) Ni value includes Co. |
||||
| Min (%) | 88.0 | 6.0 | 1.8 | |
| Max (%) | 0.25 | 8.0 | 3.2 | |
| Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.5% Ext (ksi) |
Elongation (%) |
Brinell Hardness, 3000 kg load |
|---|---|---|---|---|---|---|
| * Measured at room temperature, 68°F (20°C). | ||||||
| As Sand Cast | As Sand Cast | M01 |
60 Min for Standard 75 Typ |
28 Min for Standard 34 Typ |
10 Min for Standard 18 Typ |
140 Typ |
| Melting Point - Liquidus°F | 1840 |
|---|---|
| Melting Point - Solidus°F | 1800 |
| Densitylb/cu in. at 68°F | 0.278 |
| Specific Gravity | 7.7 |
| Electrical Conductivity% IACS at 68°F | 8 |
| Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 22.3 |
| Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 9.2 |
| Specific Heat CapacityBtu/ lb /°F at 68°F | 0.1 |
| Modulus of Elasticity in Tensionksi | 15000 |
| Casting Attribute | Level |
|---|---|
| Casting Yield | Low |
| Drossing | High |
| Effect of Section Size | Low |
| Fluidity | Medium |
| Gassing | High |
| Patternmakers Shrinkage inches per inch | 3/16 |
| Shrinkage in Solidification | High |
| Technique | Suitability |
|---|---|
| Soldering | Good |
| Brazing | Good |
| Oxyacetylene Welding | Not Recommended |
| Gas Shielded Arc Welding | Good |
| Coated Metal Arc Welding | Fair |
| Machinability Rating | 60 |
Common Fabrication Processes
No fabrication process properties for this alloy
| Treatment | Value* | Time** | ||
|---|---|---|---|---|
| * Temperature is measured in Fahrenheit. ** Time is measured in minutes. | ||||
| Stress Relief | 600 | |||
| Solution Treatment | 0 | |||
| Product Category | Product | Reason Category | Reason |
|---|---|---|---|
| Electrical | Cable Connectors | Conductivity (Electrical) | Electrical Conductivity |
| Cable Connectors | Conductivity (Thermal) | Thermal Conductivity | |
| Cable Connectors | Corrosion Resistance | Corrosion Resistance (Excellent) | |
| Cable Connectors | Mechanical Properties | High Strength | |
| Cable Connectors | Mechanical Properties | High Toughness | |
| Terminals | Conductivity (Electrical) | Electrical Conductivity | |
| Terminals | Conductivity (Thermal) | Thermal Conductivity | |
| Terminals | Corrosion Resistance | Corrosion Resistance | |
| Terminals | Friction & Wear Properties | Wear Resistance | |
| Terminals | Mechanical Properties | Fatigue Strength | |
| Terminals | Mechanical Properties | High Strength | |
| Industrial | Gears | Corrosion Resistance | Corrosion Resistance (Excellent) |
| Gears | Friction & Wear Properties | Wear Resistance | |
| Gears | Machining Properties | Machinability, Good | |
| Gears | Mechanical Properties | High Strength | |
| Valve Stems | Corrosion Resistance | Corrosion Resistance (Excellent) | |
| Valve Stems | Friction & Wear Properties | Wear Resistance | |
| Valve Stems | Mechanical Properties | High Strength | |
| Valve Stems | Mechanical Properties | Toughness | |
| Worms | Corrosion Resistance | Corrosion Resistance | |
| Worms | Corrosion Resistance | Corrosion Resistance to Salt Water | |
| Worms | Friction & Wear Properties | Wear Resistance | |
| Worms | Mechanical Properties | Fatigue Strength | |
| Worms | Mechanical Properties | High Strength |
| Form | Specific Sub-Form | Application | System | Standard | Description |
|---|---|---|---|---|---|
| As Sand Cast | Castings | ASTM | B148 | ALUMINUM BRONZE SAND CASTINGS | |
| Castings | ASTM | B763/B763M | COPPER ALLOY SAND CASTINGS FOR VALVE APPLICATIONS | ||
| Ingot | |||||
| ASTM | B30 | COPPER BASE ALLOYS IN INGOT FORM |
Corrosion Properties
No Corrosion Properties Available.