C95600
Elements | ||||
---|---|---|---|---|
Cu(1) | Ni(2) | Al | Si | |
(1) Cu + Sum of Named Elements 99.0% min. (2) Ni value includes Co. |
||||
Min (%) | 88.0 | 6.0 | 1.8 | |
Max (%) | 0.25 | 8.0 | 3.2 |
Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.5% Ext (ksi) |
Elongation (%) |
Brinell Hardness, 3000 kg load |
---|---|---|---|---|---|---|
* Measured at room temperature, 68°F (20°C). | ||||||
As Sand Cast | As Sand Cast | M01 |
60 Min for Standard 75 Typ |
28 Min for Standard 34 Typ |
10 Min for Standard 18 Typ |
140 Typ |
Melting Point - Liquidus°F | 1840 |
---|---|
Melting Point - Solidus°F | 1800 |
Densitylb/cu in. at 68°F | 0.278 |
Specific Gravity | 7.7 |
Electrical Conductivity% IACS at 68°F | 8 |
Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 22.3 |
Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 9.2 |
Specific Heat CapacityBtu/ lb /°F at 68°F | 0.1 |
Modulus of Elasticity in Tensionksi | 15000 |
Casting Attribute | Level |
---|---|
Casting Yield | Low |
Drossing | High |
Effect of Section Size | Low |
Fluidity | Medium |
Gassing | High |
Patternmakers Shrinkage inches per inch | 3/16 |
Shrinkage in Solidification | High |
Technique | Suitability |
---|---|
Soldering | Good |
Brazing | Good |
Oxyacetylene Welding | Not Recommended |
Gas Shielded Arc Welding | Good |
Coated Metal Arc Welding | Fair |
Machinability Rating | 60 |
Common Fabrication Processes
Treatment | Value* | Time** | ||
---|---|---|---|---|
* Temperature is measured in Fahrenheit. ** Time is measured in minutes. | ||||
Stress Relief | 600 | |||
Solution Treatment | 0 |
Product Category | Product | Reason Category | Reason |
---|---|---|---|
Electrical | Cable Connectors | Conductivity (Electrical) | Electrical Conductivity |
Cable Connectors | Conductivity (Thermal) | Thermal Conductivity | |
Cable Connectors | Corrosion Resistance | Corrosion Resistance (Excellent) | |
Cable Connectors | Mechanical Properties | High Strength | |
Cable Connectors | Mechanical Properties | High Toughness | |
Terminals | Conductivity (Electrical) | Electrical Conductivity | |
Terminals | Conductivity (Thermal) | Thermal Conductivity | |
Terminals | Corrosion Resistance | Corrosion Resistance | |
Terminals | Friction & Wear Properties | Wear Resistance | |
Terminals | Mechanical Properties | Fatigue Strength | |
Terminals | Mechanical Properties | High Strength | |
Industrial | Gears | Corrosion Resistance | Corrosion Resistance (Excellent) |
Gears | Friction & Wear Properties | Wear Resistance | |
Gears | Machining Properties | Machinability, Good | |
Gears | Mechanical Properties | High Strength | |
Valve Stems | Corrosion Resistance | Corrosion Resistance (Excellent) | |
Valve Stems | Friction & Wear Properties | Wear Resistance | |
Valve Stems | Mechanical Properties | High Strength | |
Valve Stems | Mechanical Properties | Toughness | |
Worms | Corrosion Resistance | Corrosion Resistance | |
Worms | Corrosion Resistance | Corrosion Resistance to Salt Water | |
Worms | Friction & Wear Properties | Wear Resistance | |
Worms | Mechanical Properties | Fatigue Strength | |
Worms | Mechanical Properties | High Strength |
Form | Specific Sub-Form | Application | System | Standard | Description |
---|---|---|---|---|---|
As Sand Cast | Castings | ASTM | B148 | ALUMINUM BRONZE SAND CASTINGS | |
Castings | ASTM | B763/B763M | COPPER ALLOY SAND CASTINGS FOR VALVE APPLICATIONS | ||
Ingot | |||||
ASTM | B30 | COPPER BASE ALLOYS IN INGOT FORM |
Corrosion Properties